Comportamento termo-dimensional de rocha artificial vítrea

Thermo-dimensional behavior of artificial vitreous stone.

Authorship

REIS, MARCELO BARCELLOS; REIS, GUILHERME DE SOUZA; REBEL, CARLOS LUCIANO GOMES; FARIA, ROMULO FURTADO; MIRANDA, RAFAEL BITTENCOURT; LÍRIO, JOSÉ LUCAS DECOTÉ DE CARVALHO; SILVA, TATIANE BRITO PERIM DA; SILVA, THAIS LEAL DA CRUZ; COSTA, ELAINE APARECIDA SANTOS CARVALHO; VIEIRA, CARLOS MAURÍCIO FONTES

REIS, MARCELO BARCELLOS

I am this author

REIS, GUILHERME DE SOUZA

I am this author

REBEL, CARLOS LUCIANO GOMES

I am this author

FARIA, ROMULO FURTADO

I am this author

MIRANDA, RAFAEL BITTENCOURT

I am this author

LÍRIO, JOSÉ LUCAS DECOTÉ DE CARVALHO

I am this author

SILVA, TATIANE BRITO PERIM DA

I am this author

SILVA, THAIS LEAL DA CRUZ

I am this author

COSTA, ELAINE APARECIDA SANTOS CARVALHO

I am this author

VIEIRA, CARLOS MAURÍCIO FONTES

I am this author

DOI

10.5151/2594-5327-43165

Downloads

Abstract

A resposta termo-dimensional é um parâmetro decisivo para a qualificação de rochas artificiais destinadas a bancadas, tampos e revestimentos internos submetidos a variações de temperatura. Neste trabalho, avaliou-se, por dilatometria, o comportamento de uma rocha artificial vítrea produzida com vidro soda-cal reciclado e matriz epóxi, comparando duas composições selecionadas por empacotamento particulado (#4 e #8) com materiais de referência: granito Branco SIENA e rocha aglomerada Branco PRIME. As formulações foram definidas por meio de planejamento simplex-centroide, densidade vibrada e tratamento estatístico, sendo processadas por prensagem térmica a 15 MPa, 90 °C e 20 min, com vácuo inicial e pós-cura. Os índices físicos foram tratados como balizadores da densificação e da conectividade dos vazios. A dilatometria mostrou que a composição #4 apresentou trajetória mais estável, com menor coeficiente de dilatação térmica linear (3,78 × 10⁻³ mm/m°C), enquanto a composição #8 exibiu maior sensibilidade dimensional (7,51 × 10⁻³ mm/m°C). Entre os materiais comparativos, o Branco SIENA apresentou 4,16 × 10⁻³ mm/m°C e o Branco PRIME, 8,48 × 10⁻³ mm/m°C. Os resultados indicam que o empacotamento, a impregnação eficiente e a baixa porosidade aberta governam diretamente a estabilidade dimensional, destacando a composição #4 como a formulação com melhor margem tecnológica.

The thermo-dimensional response is a decisive parameter for the qualification of artificial rocks intended for countertops, tabletops, and interior cladding subjected to temperature variations. In this work, the behavior of a vitreous artificial rock produced with recycled soda-lime glass and an epoxy matrix was evaluated by dilatometry, comparing two compositions selected by particulate packing (#4 and #8) with reference materials: Branco SIENA granite and Branco PRIME agglomerated rock. The formulations were defined through simplex-centroid design, vibrated density, and statistical treatment, and processed by thermal pressing at 15 MPa, 90 °C, and 20 min, with initial and post-curing vacuum. The physical indices were treated as benchmarks of densification and void connectivity. Dilatometry showed that composition #4 exhibited a more stable trajectory, with a lower linear thermal expansion coefficient (3.78 × 10⁻³ mm/m°C), while composition #8 showed greater dimensional sensitivity (7.51 × 10⁻³ mm/m°C). Among the comparative materials, SIENA White presented 4.16 × 10⁻³ mm/m°C and PRIME White, 8.48 × 10⁻³ mm/m°C. The results indicate that packing, efficient impregnation, and low open porosity directly govern dimensional stability, highlighting composition #4 as the formulation with the best technological margin.

Keywords

Dilatometria, Estabilidade dimensional, Rocha artificial vítrea, Vidro soda-cal

Dilatometry, Dimensional stability, Soda-lime glass, Vitreous artificial stone