Title

COMPORTAMENTO TRIBOCORROSIVO DE AÇOS FERRAMENTA PARA APLICAÇÃO EM EQUIPAMENTOS DE AGLOMERAÇÃO DE MINÉRIO DE FERRO

TRIBOCORROSIVE BEHAVIOR OF TOOL STEELS FOR APPLICATION IN AN IRON ORE AGGLOMERATION EQUIPMENT

Authorship

RIBEIRO, NIRVANA CECILIA; SILVA, RENATO CHAVES PEREIRA DA; ANDRADE, JOSÉ LUIZ PENA; BRISENO, CÍNTIA BRAGA; VIÁFARA, CRISTIAN; MAMBRINI, RAQUEL VIEIRA; PENAGOS, JOSÉ JIMMY

RIBEIRO, NIRVANA CECILIA

I am this author

SILVA, RENATO CHAVES PEREIRA DA

I am this author

ANDRADE, JOSÉ LUIZ PENA

I am this author

BRISENO, CÍNTIA BRAGA

I am this author

VIÁFARA, CRISTIAN

I am this author

MAMBRINI, RAQUEL VIEIRA

I am this author

PENAGOS, JOSÉ JIMMY

I am this author

DOI

10.5151/2594-357X-41320

Downloads

Abstract

O COMPORTAMENTO TRIBOCORROSIVO DE DOIS AçOS FERRAMENTA, O AçO AISI H13 E O AçO AISI D2, FOI INVESTIGADO UTILIZANDO O EQUIPAMENTO MILLER SEGUINDO METODOLOGIA ADAPTADA DA NORMA ASTM G75. FORAM UTILIZADOS DOIS TIPOS DE POLPAS DE MINéRIO DE FERRO E UMA DE AREIA NORMAL BRASILEIRA (IPT) COM GRANULOMETRIA NA FAIXA DE 0,30-0,15 MM. O AçO D2 (61 HRC), CARACTERIZADO PELA PRESENçA DE CARBETOS DE CROMO EM MATRIZ MARTENSíTICA, DEMONSTROU UM DESEMPENHO TRIBOLóGICO SUPERIOR QUANDO COMPARADO AO AçO H13, AçO MARTENSíTICO COM DUREZA DE 52 HRC. TOMANDO COMO REFERêNCIA A POLPA DE AREIA, O AçO D2 APRESENTOU MENOR DESGASTE, SENDO 1,5 VEZES MENOR COM A POLPA DO MINéRIO A1 E 5 VEZES MENOR COM A POLPA DO MINéRIO A2. EM RELAçãO à ABRASIVIDADE DAS POLPAS, FOI OBSERVADA A CLASSIFICAçãO: AREIA>A1>A2. AS IMAGENS DAS SUPERFíCIES DE DESGASTE MOSTRARAM MENOR PRESENçA DE CORROSãO NO AçO D2 COMPARADO AO H13. ADICIONALMENTE, AMBOS OS MATERIAIS, APRESENTARAM MAIOR TENDêNCIA à CORROSãO QUANDO DESGASTADO COM AS POLPAS DE MINéRIO DE FERRO. VISANDO O AUMENTO DE VIDA úTIL DE EQUIPAMENTOS DE MINERAçãO, O AçO AISI D2 APRESENTOU ELEVADA RESISTêNCIA AO DESGASTE, COM PERSPECTIVA DE ESCALABILIDADE PARA TESTES EM CAMPO.

THE TRIBOCORROSIVE BEHAVIOR OF TWO TOOL STEELS, AISI H13 AND D2 STEELS, WAS INVESTIGATED USING MILLER EQUIPMENT USING A METHODOLOGY ADAPTED FROM THE ASTM G75 STANDARD. TWO TYPES OF IRON ORE SLURRIES WERE USED, AND ANOTHER ONE OF A NORMAL BRAZILIAN SAND (IPT) WITH A GRAIN SIZE OF 0.30-0.15 MM. D2 STEEL (61 HRC), CHARACTERIZED BY THE PRESENCE OF CHROMIUM CARBIDES IN A MARTENSITIC MATRIX, SHOWED SUPERIOR TRIBOLOGICAL PERFORMANCE WHEN COMPARED TO H13 STEEL, A MARTENSITIC STEEL WITH A HARDNESS OF 52 HRC. USING THE SAND SLURRY AS A REFERENCE D2 STEEL SHOWED LESS WEAR, BEING 1.5 TIMES LESS WITH THE A1 ORE SLURRY AND 5 TIMES LESS WITH THE A2 ORE SLURRY. THE CLASSIFICATION WAS OBSERVED FOR ABRASIVENESS OF THE SLURRIES: SAND>A1>A2. THE IMAGES OF THE WEAR SURFACES SHOWED LESS CORROSION ON D2 STEEL COMPARED TO H13. IN ADDITION, BOTH MATERIALS SHOWED A GREATER TREND TO CORROSION IN WEAR TESTS WITH IRON ORE SLURRIES. IN THE AIM OF INCREASING THE USEFUL LIFE OF AN IRON ORE AGGLOMERATION EQUIPMENT, AISI D2 STEEL SHOWED HIGH WEAR RESISTANCE, WITH THE PROSPECT OF SCALABILITY FOR FIELD TESTS.

Keywords

tribocorrosão; desgaste abrasivo; aço ferramenta; equipamento Miller

tribocorrosion; abrasive wear; tool steel; Miller machine.