COMPÓSITOS COM FIBRAS DE PALHA DA COSTA (RAPHIA VINIFERA) EM MATRIZ POLIMÉRICA: ANÁLISE DAS PROPRIEDADES FÍSICAS, MECÂNICA DE TRAÇÃO E DE FLAMABILIDADE

COMPOSITES WITH COASTAL STRAW FIBERS (RAPHIA VINIFERA) IN POLYMER MATRIX: ANALYSIS OF PHYSICAL PROPERTIES, TENSILE MECHANICS AND FLAMMABILITY

Authorship

DOI

10.5151/2594-4711-42037

Downloads

0 Downloads

Abstract

Este trabalho promoveu fabricar compósitos com a fibra de palha da costa (Raphia Vinifera) longa em matriz polimérica, utilizando diferentes frações mássicas para avaliar as propriedades físicas, mecânica de tração e de flamabilidade. Após adquirir as fibras, realizou-se a massa especifica da fibra pelo método do picnômetro e deu início a fabricação em um molde de silicone, com compressão, de matriz polimérica com 1% de iniciador e as frações em massa de 1%,3% e 5% da fibra. Depois da fabricação dos corpos de prova, foram submetidos ensaios físicos de absorção de água (AA)- ASTM D570, porosidade aparente (PA)-ASTM D2734 e massa específica aparente (MEA)-ASTM D792, ensaios de tração (ASTM D638) e flamabilidade (ASTM D635). Nos ensaios físicos de AA e PA os compósitos obtiveram resultados superiores quando comparados com a matriz plena e o MEA permaneceu coerente com as literaturas pesquisadas. No ensaio de tração as fibras atuaram como reforço, pois obtiveram resultados superiores a matriz de comparação, no ensaio de flamabilidade apresentaram taxas de propagação inferiores ao limite estabelecido pelas normas ASTM D635 e CONTRAN 498. Por fim, o trabalho de compósitos poliméricos com fibras de palha de costa obteve resultados satisfatórios, diminuindo os resíduos e/ou materiais sintéticos e colocando uma alternativa sustentável de fibra natural contribuindo com o meio ambiente.

 

THIS WORK AIMED TO MANUFACTURE COMPOSITES WITH LONG COASTAL STRAW FIBER (RAPHIA VINIFERA) IN A POLYMER MATRIX, USING DIFFERENT MASS FRACTIONS TO EVALUATE THE PHYSICAL, MECHANICAL, TENSILE AND FLAMMABILITY PROPERTIES. AFTER ACQUIRING THE FIBERS, THE SPECIFIC MASS OF THE FIBER WAS DETERMINED BY THE PYCNOMETER METHOD AND THE MANUFACTURE BEGAN IN A SILICONE MOLD, WITH COMPRESSION, OF A POLYMER MATRIX WITH 1% INITIATOR AND THE MASS FRACTIONS OF 1%, 3% AND 5% OF THE FIBER. AFTER THE FABRICATION OF THE TEST SPECIMENS, THEY WERE SUBJECTED TO PHYSICAL TESTS OF WATER ABSORPTION (AA) - ASTM D570, APPARENT POROSITY (AP) - ASTM D2734 AND APPARENT SPECIFIC MASS (ASM) - ASTM D792, TENSILE TESTS (ASTM D638) AND FLAMMABILITY (ASTM D635). IN THE PHYSICAL TESTS OF AA AND AP, THE COMPOSITES OBTAINED SUPERIOR RESULTS WHEN COMPARED TO THE FULL MATRIX AND THE ASM REMAINED CONSISTENT WITH THE LITERATURE RESEARCHED. IN THE TENSILE TEST, THE FIBERS ACTED AS REINFORCEMENT, AS THEY OBTAINED RESULTS SUPERIOR TO THE COMPARISON MATRIX. IN THE FLAMMABILITY TEST, THEY PRESENTED PROPAGATION RATES LOWER THAN THE LIMIT ESTABLISHED BY ASTM D635 AND CONTRAN 498 STANDARDS. FINALLY, THE WORK OF POLYMER COMPOSITES WITH FIBERS FROM COASTAL STRAW OBTAINED SATISFACTORY RESULTS, REDUCING WASTE AND/OR SYNTHETIC MATERIALS AND PROVIDING A SUSTAINABLE ALTERNATIVE TO NATURAL FIBER, CONTRIBUTING TO THE ENVIRONMENT.

Keywords

Fibras naturais, Materiais compósitos, Fibras palha da costa.

How to cite

FERREIRA, KAUÃ RAMON MOURA; FERNANDES, JENNIFER FERREIRA; BARBOSA, EMILLI RAFAELA DA CONCEIçãO; LIMA, HAIANNY BEATRIZ SARAIVA; RODRIGUES, EMERSON CARDOSO; MACêDO, EMANUEL NEGRãO; COSTA, DEIBSON SILVA DA. COMPÓSITOS COM FIBRAS DE PALHA DA COSTA (RAPHIA VINIFERA) EM MATRIZ POLIMÉRICA: ANÁLISE DAS PROPRIEDADES FÍSICAS, MECÂNICA DE TRAÇÃO E DE FLAMABILIDADE, p. 187-196. In: 23nd Enemet - National Meeting of Metallurgical, Materials and Mining Engineering Students, São Paulo, Brasil, 2025.