Title

COMPÓSITOS COM FIBRAS DE AÇAÍ (EUTERPE OLERACEA) EM MATRIZ POLIMÉRICA: ANÁLISE DAS PROPRIEDADES FÍSICAS, MECÂNICA E FRACTOGRÁFICA

COMPOSITES WITH AÇAÍ FIBERS (EUTERPE OLERACEA) IN POLYMER MATRIX: ANALYSIS OF PHYSICAL, MECHANICAL AND FRACTOGRAPHIC PROPERTIES

Authorship

FERNANDES, JENNIFER FERREIRA; MONTEIRO, MANOEL VINÍCIUS FRANÇA; SOUSA, ANA PAULA SOUZA DE; LIMA, HAIANNY BEATRIZ SARAIVA; ESTUMANO, DIEGO CARDOSO; RODRIGUES, EMERSON CARDOSO; COSTA, DEIBSON SILVA DA

FERNANDES, JENNIFER FERREIRA

I am this author

MONTEIRO, MANOEL VINÍCIUS FRANÇA

I am this author

SOUSA, ANA PAULA SOUZA DE

I am this author

LIMA, HAIANNY BEATRIZ SARAIVA

I am this author

ESTUMANO, DIEGO CARDOSO

I am this author

RODRIGUES, EMERSON CARDOSO

I am this author

COSTA, DEIBSON SILVA DA

I am this author

DOI

10.5151/2594-4711-41143

Downloads

Abstract

O TRABALHO APRESENTA UM DOS FRUTOS MAIS IMPORTANTES DA AMAZôNIA, O AçAí, E LEVANTA A QUESTãO DO DESCARTE INADEQUADO DOS CAROçOS APóS O CONSUMO DA SUA POLPA. ESSES CAROçOS PODEM SER APROVEITADOS PARA A EXTRAçãO DAS FIBRAS, PODENDO SER UTILIZADAS NA FABRICAçãO DE COMPóSITOS. ASSIM, O ESTUDO OBJETIVOU CARACTERIZAR MORFOLOGICAMENTE E DETERMINAR A MASSA ESPECíFICA DA FIBRA DE AçAí, VISANDO A FABRICAçãO DE COMPóSITOS POLIMéRICOS COM DIFERENTES FRAçõES MáSSICAS (1%, 2% E 3%), PARA ANáLISE DAS PROPRIEDADES FíSICAS (MEA, PA E AA) MECâNICA DE TRAçãO, SEGUIDA DE ANáLISE FRACTOGRáFICA. AS FIBRAS FORAM EXTRAíDAS MANUALMENTE E SUA MORFOLOGIA FOI ANALISADA POR MEIO DO MICROSCóPIO ELETRôNICO DE VARREDURA (MEV). OS COMPóSITOS FORAM FABRICADOS PELO MéTODO MANUAL (HAND LAY UP), UTILIZANDO MATRIZ POLIéSTER ORTOFTáLICA E INICIADOR BUTANOX (1% V/V) E UMA COMPRESSãO NOS CORPOS DE PROVA. A ANáLISE MORFOLóGICA REVELOU RUGOSIDADE E IMPERFEIçõES NAS FIBRAS. A MASSA ESPECíFICA APRESENTOU MéDIA DE 1,09 G/CM3. NOS ENSAIOS FíSICOS, A ABSORçãO DE áGUA (AA) E POROSIDADE APARENTE (PA) AUMENTARAM COM ADIçãO DAS FIBRAS NA MATRIZ E A MASSA ESPECíFICA APARENTE (MEA) PERMANECEU SIMILAR. NO ENSAIO DE TRAçãO, AS FIBRAS ATUARAM COMO MATERIAL DE ENCHIMENTO, POIS A RESISTêNCIA NãO ULTRAPASSOU DA MATRIZ, NO ENTANTO ESTE FATO PODE PROMOVER A REDUçãO DO USO DO POLíMERO, REDUZINDO SEU IMPACTO AMBIENTAL.

THE WORK PRESENTS ONE OF THE MOST IMPORTANT FRUITS FROM THE AMAZôNIA, AçAí, AND RAISES THE ISSUE OF INADEQUATE DISPOSAL OF THE SEEDS AFTER CONSUMING ITS PULP. THESE LUMPS CAN BE USED TO EXTRACT FIBERS, WHICH CAN BE USED IN THE MANUFACTURE OF COMPOSITES. THUS, THE STUDY AIMED TO CHARACTERIZE MORPHOLOGICALLY AND DETERMINE THE SPECIFIC MASS OF AçAí FIBER, AIMING TO MANUFACTURE POLYMER COMPOSITES WITH DIFFERENT MASS FRACTIONS (1%, 2% AND 3%), FOR ANALYSIS OF PHYSICAL PROPERTIES (MEA, PA AND AA) TRACTION MECHANICS, FOLLOWED BY FRACTOGRAPHIC ANALYSIS. THE FIBERS WERE EXTRACTED MANUALLY AND THEIR MORPHOLOGY WAS ANALYZED USING THE SCANNING ELECTRON MICROSCOPE (SEM). THE COMPOSITES WERE MANUFACTURED BY THE MANUAL METHOD (HAND LAY UP), USING ORTHOPHTHALIC POLYESTER MATRIX AND BUTANOX INITIATOR (1% V/V) AND COMPRESSION ON THE TEST SPECIMENS. MORPHOLOGICAL ANALYSIS REVEALED ROUGHNESS AND IMPERFECTIONS IN THE FIBERS. THE SPECIFIC MASS PRESENTED AN AVERAGE OF 1.09 G/CM3. IN PHYSICAL TESTS, WATER ABSORPTION (AA) AND APPARENT POROSITY (PA) INCREASED WITH THE ADDITION OF FIBERS TO THE MATRIX AND THE APPARENT SPECIFIC MASS (MEA) REMAINED SIMILAR. IN THE TENSILE TEST, THE FIBERS ACTED AS FILLING MATERIAL, AS THE RESISTANCE DID NOT EXCEED THAT OF THE MATRIX, HOWEVER THIS FACT CAN PROMOTE A REDUCTION IN THE USE OF THE POLYMER, REDUCING ITS ENVIRONMENTAL IMPACT.

Keywords

fruto da Amazônia; fibras naturais; sustentabilidade

Amazon fruit; natural fibers; sustainability.