Title

COMPÓSITOS DE RESINA EPÓXI INCORPORADA COM FIBRA DE SISAL – PROPRIEDADES MECÂNICAS E CARACTERISTICAS DE FRATURA

SISAL FIBER INCORPORATED EPOXY MATRIX COMPOSITES – MECHANICAL PROPERTIES AND FRACTURE CHARACTERISTICS

Authorship

Inácio, Wellington Pereira; Monteiro, Sergio Neves; Lopes, Felipe Perissé Duarte

Inácio, Wellington Pereira

I am this author

Monteiro, Sergio Neves

I am this author

Lopes, Felipe Perissé Duarte

I am this author

DOI

10.5151/2594-5327-16460

Downloads

Abstract

O comportamento mecânico em flexão de compósitos poliméricos reforçados com fibras alinhadas de sisal ainda não havia sido estudado para a matriz epóxi. O objetivo deste trabalho foi investigar as propriedades mecânicas e as características da fratura de compósitos com matriz epoxidica incorporada com até 35% de fibras de sisal. Fibras de sisal, comercialmente obtidas, foram colocadas de maneira alinhada, ao longo de um molde utilizado para a fabricação de compósitos juntamente com resina epóxi misturada ao endurecedor trietileno tetramina (TETA). Após cura a 25°C por um dia, uma nova pós-cura foi feita e corpos de prova de flexão foram ensaiados até a ruptura. A superfície de fratura foi analisada por microscopia eletrônica de varredura. Obteve-se um aumento na resistência à flexão dos compósitos até a fração incorporada de 35% em volume de fibras de sisal. Este efeito de reforço nos compósitos pôde ser interpretado através da observação do processo de interação fibra/matriz durante a propagação das trincas na fratura.

The flexural mechanical behavior of epoxy composites reinforced with sisal fibers has not yet been studied for the epoxy matrix. The objective of this work was to investigate the mechanical properties and fracture characteristics of epoxy matrix composites incorporated with up to 35% in volume of sisal fibers. Sisal fibers, commercially available, were aligned in a mold used for the manufacture of composite with ortophtalic polyester resin mixed with triethylene tetramine (TETA) hardener. After curing at 25°C for one day other post-cure was done. Bend specimens were tested until rupture. The fracture surface was examined by scanning electron microscopy. An increase in the flexural resistance of composites with up to 35% of sisal fibers was obtained. This effect of strengthening in the composites was interpreted through the observation of the fiber/matrix interaction during cracks propagation in the fracture.

Keywords

Fibra de sisal; Compósito polimérico; Ensaio de flexão; Características da fratura.

Sisal fiber; Polymer composites; Bending test; Fracture characteristics.