Title

DESEMPENHO MECÂNICO EM COMPÓSITOS ENSAIADOS COM 10, 20 E 30%VOL DE FIBRAS CONTINUAS SOB CARREGAMENTO COMPRESSIVO A 0° E 90°

MECHANICAL PERFORMANCE OF COMPOSITES TESTED WITH 10, 20, AND 30%VOL OF CONTINUOUS FIBERS UNDER COMPRESSIVE LOADING AT 0° AND 90°

Authorship

DOI

10.5151/2594-5327-42095

Downloads

0 Downloads

Abstract

Este artigo reporta os resultados investigativos referentes aos compósitos poliméricos fibrosos preparados por moldagem manual com teores de 10, 20 e 30%vol de fibras extraídas da casca da árvore amazônica matamatá. Posteriormente à fabricação, os compósitos foram ensaiados sob carregamento compressivo com orientação a 0° e 90°. Logo, as maiores resistências testadas são para os CPs 20%vol, resultou em 150,20 ± 10,57 contra 80,61 ± 4,47 MPa.cm3/g a 0° e 90°, respectivamente, corroborando um comportamento predominantemente frágil para os compósitos investigados, conforme denotado pelas micrografias. Portanto, esses resultados demonstraram que adicionar fibras em teores mais elevados, contribui para a fragilidade microestrutural, o que estar diretamente correlacionado com a baixa dispersão, e principalmente, com a orientação das amostras testadas a 0° e 90°.

 

THIS ARTICLE REPORTS THE INVESTIGATIVE RESULTS CONCERNING FIBROUS POLYMER COMPOSITES PREPARED BY HAND LAY-UP MOLDING WITH FIBER CONTENTS OF 10, 20, AND 30% BY VOLUME, USING FIBERS EXTRACTED FROM THE BARK OF THE AMAZONIAN MATAMATá TREE. FOLLOWING FABRICATION, THE COMPOSITES WERE TESTED UNDER COMPRESSIVE LOADING AT 0° AND 90° ORIENTATIONS. THE BEST MECHANICAL PERFORMANCE WAS OBSERVED AT 20%VOL, YIELDING VALUES OF 150.20 ± 10.57 AND 80.61 ± 4.47 MPA·CM³/G AT 0° AND 90°, RESPECTIVELY, INDICATING A PREDOMINANTLY BRITTLE BEHAVIOR AS SHOWN IN THE MICROGRAPHS. THEREFORE, THESE RESULTS DEMONSTRATE THAT INCREASING THE FIBER CONTENT LEADS TO GREATER MICROSTRUCTURAL FRAGILITY, WHICH IS DIRECTLY CORRELATED WITH POOR FIBER DISPERSION AND, MORE IMPORTANTLY, WITH THE SAMPLE ORIENTATION DURING TESTING AT 0° AND 90°.

Keywords

Compósito polimérico, Fibra natural, Matriz de poliéster

Polymeric composite, natural fiber, polyester matrix

How to cite

ROSA, DIEMISON LIRA SANTA; SOARES, EDSON MIRANDA; SILVA, ALISSON CLAY RIOS DA; MONTEIRO, SERGIO NEVES; CANDIDO, VERONICA SCARPINI. DESEMPENHO MECÂNICO EM COMPÓSITOS ENSAIADOS COM 10, 20 E 30%VOL DE FIBRAS CONTINUAS SOB CARREGAMENTO COMPRESSIVO A 0° E 90°, p. 912-927. In: 78th ABM Annual Congress - International, São Paulo, Brasil, 2025.