DESEMPENHO MECÂNICO SOB TRAÇÃO EM COMPÓSITOS DE POLIÉSTER COM 5%, 15% E 25% DE FIBRAS NATURAIS

MECHANICAL PERFORMANCE UNDER TRACTION OF POLYESTER COMPOSITES WITH 5%, 15%, AND 25% NATURAL FIBERS

Authorship

ROSA, DIEMISON LIRA SANTA; CANDIDO, VERÔNICA SCARPINI; SILVA, ALISSON CLAY RIOS DA; MONTEIRO, SERGIO NEVES

ROSA, DIEMISON LIRA SANTA

I am this author

CANDIDO, VERÔNICA SCARPINI

I am this author

SILVA, ALISSON CLAY RIOS DA

I am this author

MONTEIRO, SERGIO NEVES

I am this author

DOI

10.5151/2594-5327-41230

Downloads

Abstract

ESTE ARTIGO INVESTIGA O IMPACTO DA INCORPORAçãO DE FIBRAS NATURAIS NAS PROPRIEDADES MECâNICAS DE COMPOSTOS DE MATRIZ DE POLIéSTER POR MEIO DO ENSAIO DE TRAçãO E ANáLISES DE MEV. OS RESULTADOS MOSTRAM QUE OS COMPóSITOS SEM FIBRAS POSSUEM RESISTêNCIA à TRAçãO DE 46.940 MPA. A ADIçãO DE 5%, 15% E 25% DE FIBRAS RESULTA EM RESISTêNCIAS DE 40.967 MPA, 43.020 MPA E 34.073 MPA, RESPECTIVAMENTE. A ANOVA CONFIRMA DIFERENçAS SIGNIFICATIVAS ENTRE OS GRUPOS DOS COMPóSITOS COM (P < 0,05). O MóDULO ELáSTICO SOB TENSãO FOI DE 1,077 GPA PARA 1,102 GPA COM 5% DE FIBRAS, E PARA 1,127 GPA COM 15%, MAS DIMINUíDO PARA 1,010 GPA COM 25%. A DEFORMAçãO INICIAL CAIU DE 0,05515% (0% FIBRAS) PARA 0,04449% (5% FIBRAS), ESTABILIZANDO EM 0,04515% COM 15%. O ESTUDO CONCLUI QUE A ADIçãO DE FIBRAS NATURAIS PODE MELHORAR AS PROPRIEDADES EM TRAçãO ATé UM PONTO óTIMO, A ADIçãO DE FIBRAS EM FRAçõES VOLUMéTRICAS INFERIORES E SUPERIORES A 15%, NECESSITAM DE TRATAMENTOS PARA MELHORAR A ADESãO DAS FIBRAS NA MATRIZ E O DESEMPENHO MECâNICO DOS COMPóSITOS.

THIS ARTICLE INVESTIGATES THE IMPACT OF INCORPORATING NATURAL FIBERS ON THE MECHANICAL PROPERTIES OF POLYESTER MATRIX COMPOSITES THROUGH TENSILE TEST AND SEM ANALYSIS. THE RESULTS SHOW THAT COMPOSITES WITHOUT FIBERS HAVE A TENSILE STRENGTH OF 46.940 MPA. THE ADDITION OF 5%, 15%, AND 25% FIBERS RESULTS IN STRENGTHS OF 40.967 MPA, 43.020 MPA, AND 34.073 MPA, RESPECTIVELY. ANOVA CONFIRMS SIGNIFICANT DIFFERENCES BETWEEN THE COMPOSITE GROUPS (P < 0.05). THE TENSILE MODULUS WAS 1.077 GPA FOR COMPOSITES WITHOUT FIBERS, 1.102 GPA WITH 5% FIBERS, 1.127 GPA WITH 15%, BUT DECREASED TO 1.010 GPA WITH 25% FIBERS. THE INITIAL STRAIN DECREASED FROM 0.05515% (0% FIBERS) TO 0.04449% (5% FIBERS), STABILIZING AT 0.04515% WITH 15% FIBERS. THE STUDY CONCLUDES THAT ADDING NATURAL FIBERS CAN IMPROVE TENSILE PROPERTIES UP TO AN OPTIMAL POINT; ADDING FIBERS IN VOLUME FRACTIONS BELOW AND ABOVE 15% REQUIRES TREATMENTS TO ENHANCE FIBER-MATRIX.

Keywords

Fibra natural; Compósitos poliéster; Propriedades mecânicas

Natural fiber; Polyester composites; Mechanical properties