DESENVOLVIMENTO DE VERGALHÃO EM ROLO MICROLIGADO DE ALTA RESISTÊNCIA

DEVELOPMENT OF HIGH STRENGTH MICROALLOYED COILED REBAR

Authorship

Lino, Roney Eduardo; Oliveira, Felipe Gabriel; Silva, Letícia Barbosa; Reis, Luciano de Castro; Lima, Ermani; Costa, Joaquim; Barbosa, Ronaldo

Lino, Roney Eduardo

I am this author

Oliveira, Felipe Gabriel

I am this author

Silva, Letícia Barbosa

I am this author

Reis, Luciano de Castro

I am this author

Lima, Ermani

I am this author

Costa, Joaquim

I am this author

Barbosa, Ronaldo

I am this author

DOI

10.5151/1983-4764-30796

Downloads

Abstract

As ocorrências recentes de terremotos em diversos países têm incentivado o desenvolvimento de vergalhão com características sísmicas, ou seja, que apresente elevada resistência mecânica sem que a ductilidade seja deteriorada. Este trabalho propôs uma abordagem investigativa dos principais fenômenos metalúrgicos atuantes no processo de laminação a quente de vergalhão em rolo Ø20 mm. Foi utilizado um modelo matemático de evolução microestutural com equações capazes de prever a quantidade de elementos microligantes ao longo do processo, a cinética de precipitação e o comportamento do tamanho de grão austenítico durante todo o tempo de laminação. Os resultados industriais de microestrutura e propriedades mecânicas convergiram com os resultados previstos pelo modelo. Com combinação do modelo matemático com testes industriais foi possível obter vergalhão com limite de escoamento superior a 600 MPa e alongamento de 15 %.

Recent earthquakes in several countries have encouraged the development of rebar with seismic characteristics, that is, high mechanical resistance without the ductility being deteriorated. This work proposes an investigative approach of the main metallurgical phenomena active in the hot rolling process of Ø20 mm coil rebar. A mathematical model for microstructure evolution was used to predict the amount of microalloying elements which were either precipitated or in solution during the course of the process, the kinetics of precipitation and the behavior of the austenitic grain size during rolling. Industry trials were run according to guidelines given by the proposed model. Industry results of microstructure and mechanical properties converged to results predicted by the model. Combination of metallurgical modeling with industry trials resulted in yield strength in rebars with excess of 600 MPa and elongation 15 %.

Keywords

Vergalhão de alta resistência, Aços longos microligados, Processo termomecânico

High strength rebar, Microlloyed long steels, Thermomechanical process