Title

DETERMINAÇÃO DA INFLUÊNCIA DA COMPOSIÇÃO DAS MISTURAS DESSULFURANTES DE FERRO-GUSA USANDO A TERMODINÂMICA COMPUTACIONAL

DETERMINATION OF THE INFLUENCE OF HOT METAL DESULFURIZING MIXTURES COMPOSITION USING COMPUTATIONAL THERMODYNAMICS

DOI

10.5151/1982-9345-28037

Downloads

Abstract

Devido ao fato que a exigência por menores teores de enxofre em alguns tipos de aços, torna-se interessante investigar a eficiência na dessulfuração dos materiais já conhecidos com matérias primas alternativas. Duas dessas novas matérias primas que podem ser utilizadas no processo de dessulfuração são o resíduo de mármore e a sodalita. Desta forma, o presente trabalho tem como objetivo avaliar a eficiência de dessulfuração em ferro-gusa por misturas contendo resíduo de mármore, sodalita e agentes dessulfurantes convencionalmente utilizados. Os testes foram realizados a 1400°C, em uma atmosfera inerte (Ar) com agitação constante. Os testes experimentais mostraram que 50 a 90% da dessulfuração ocorreu em até 15 minutos. As misturas contendo fluorita foram os que apresentaram maior eficiência de dessulfuração. A adição de sodalita ocasionou uma queda na eficiência de dessulfuração.

 

Due to fact that lesser sulfur content is required in steel, investigate the desulfurization efficiency from alternative raw materials become interesting. Two of these raw materials that can be used in the desulfurization process are marble waste and sodalite. Thus, the aim of this paper is to evaluate the desulfurization efficiency in pig iron for mixtures containing marble waste, sodalite and desulfurizing agents conventionally used. The tests were performed at 1400°C. Argon was used to create an inert atmosphere. In addition, the bath was agitated constantly. The essays showed that 50 to 90% of sulfur was removed up to 15 minutes. The mixtures containing fluorite showed higher desulfurization efficiency. The addition of sodalite caused a decrease on desulfurization efficiency.

Keywords

Dessulfuração, Sodalita, Resíduo de mármore

Desulfurization, Sodalite, Marble waste

How to refer

Pezzin, Rodrigo de Oliveira; Soares, Silas Gambarine; Oliveira, Heitor Cristo Clem de; Oliveira, Sábata Marla Reis Durães; Grillo, Felipe Fardin; Junca, Eduardo; Oliveira, José Roberto de. DETERMINAÇÃO DA INFLUÊNCIA DA COMPOSIÇÃO DAS MISTURAS DESSULFURANTES DE FERRO-GUSA USANDO A TERMODINÂMICA COMPUTACIONAL , p. 684-692. In: 47th Steelmaking Seminar - International, Rio de Janeiro, 2016.