DETERMINAÇÃO EXPERIMENTAL DAS RELAÇÕES DE FASES DO SISTEMA NB-TI-SI NA SEÇÃO ISOTÉRMICA A 1.200°C

EXPERIMENTAL DETERMINATION OF NB-TI-SI SYSTEM PHASE RELATIONS IN 1,200°C ISOTHERMAL SECTION

Authorship

Gigolotti, João Carlos Jânio; Joubert, Jean-Marc; Coelho, Gilberto Carvalho; Nunes, Carlos Angelo; Suzuki, Paulo Atsushi; Cardoso, Bruna Sousa; Pereira, Ramon Durço

Gigolotti, João Carlos Jânio

I am this author

Joubert, Jean-Marc

I am this author

Coelho, Gilberto Carvalho

I am this author

Nunes, Carlos Angelo

I am this author

Suzuki, Paulo Atsushi

I am this author

Cardoso, Bruna Sousa

I am this author

Pereira, Ramon Durço

I am this author

DOI

10.5151/1516-392X-26890

Downloads

Abstract

Foram estudadas experimentalmente as relações de fases do sistema Nb-Ti-Si na seção isotérmica a 1200 °C. Ligas fundidas em forno a arco em atmosfera de argônio a partir de Nb, Ti e Si de alta pureza (˃ 99,9 %), foram tratadas termicamente a 1200 °C durante 264 h em forno tubular, em atmosfera de argônio, encapsuladas em tubos de quartzo. As ligas tiveram sua microestrutura caracterizada por difração de raios-X, microscopia eletrônica no modo elétrons retroespalhados e por microsonda. Ficaram determinados os campos ternários Nb5Si3 + (Nb, Ti)3Si + (Nb, Ti, Si), Nb5Si3 + (Nb, Ti)3Si + Ti5Si3, Ti5Si3 + (Nb, Ti)3Si + (Nb, Ti, Si), Nb5Si3 + Ti5Si4 + Ti5Si3, Nb5Si3 + Ti5Si4 + NbSi2, NbSi2 + Ti5Si4 + TiSi, NbSi2 + TiSi2 + TiSi e NbSi2 + TiSi2 + SiSS. Existe boa concordância dos resultados com as propostas calculadas e experimentais existentes na literatura para essa seção isotérmica do sistema Nb-Ti-Si. Pequenas alterações composicionais são sugeridas para a locação dos campos ternários observados.

We studied experimentally the phase relationship of the system Nb-Ti-Si in the isothermal section at 1200 °C. Alloys cast in arc furnace, under argon atmosphere, from Nb, Ti and Si of high purity (˃ 99.9%), were heat treated at 1200 °C for 264 h in a tubular furnace, under argon atmosphere, encapsulated in quartz pipes. The alloys had their microstructure characterized by X-ray diffractometry, scanning electron microscopy in backscattered electrons mode and electron beam microprobe analysis. Seven ternary regions were determined, Nb5Si3 + (Nb, Ti)3Si + (Nb, Ti, Si), Nb5Si3 + (Nb, Ti)3Si + Ti5Si3, Ti5Si3 + (Nb, Ti)3Si + (Nb, Ti, Si), Nb5Si3 + Ti5Si4 + Ti5Si3, Nb5Si3 + Ti5Si4 + NbSi2, NbSi2 + Ti5Si4 + TiSi, NbSi2 + TiSi2 + TiSi e NbSi2 + TiSi2 + SiSS. There is good agreement of the results with the calculated and experimental proposals in the literature for this isothermal section of Nb-Ti-Si system. Small compositional changes are suggested for the location of the observed ternary fields.

Keywords

Diagrama de fases, Nb-Ti-Si, Seção isotérmica

Phase diagram, Nb-Ti-Si, Isothermal section