DETERMINAÇÃO DAS PROPRIEDADES MECÂNICAS DE COMPÓSITOS DE MATRIZ POLIMÉRICA COM ADIÇÃO DE RESÍDUO DO PROCESSO BAYER

DETERMINATION OF THE MECHANICAL PROPERTIES OF POLYMER MATRIX COMPOSITES WITH THE ADDITION OF WASTE FROM THE BAYER

Authorship

SOUZA, SARAH GABRIELLY BRANDAO DE; SOUSA, PALOMA SUELLEN LIMA DE; NASCIMENTO, JOELLY VERA; BARBOSA, DAMARES DA CRUZ; ROSA, DIEMISON LIRA SANTA; CANDIDO, VERÔNICA SCARPINI; SILVA, ALISSON CLAY RIOS DA

SOUZA, SARAH GABRIELLY BRANDAO DE

I am this author

SOUSA, PALOMA SUELLEN LIMA DE

I am this author

NASCIMENTO, JOELLY VERA

I am this author

BARBOSA, DAMARES DA CRUZ

I am this author

ROSA, DIEMISON LIRA SANTA

I am this author

CANDIDO, VERÔNICA SCARPINI

I am this author

SILVA, ALISSON CLAY RIOS DA

I am this author

DOI

10.5151/2594-4711-41579

Downloads

Abstract

O DESENVOLVIMENTO DE NOVOS MATERIAIS QUE UTILIZEM MATéRIAS-PRIMAS ORIUNDAS DE RESíDUOS INDUSTRIAIS, TORNAM-SE PLEITEáVEIS PARA APLICAçõES EM DIVERSAS áREAS INDUSTRIAIS, VISANDO A OTIMIZAçãO E MELHOR UTILIZAçãO DESSES INSUMOS. A LAMA VERMELHA, ADVINDA DO PROCESSO DE OBTENçãO DO ALUMíNIO, é UM RESíDUO INDUSTRIAL ABUNDANTE E POUCO DESTINADO A REUTILIZAçãO OU REAPROVEITAMENTO. DESSA FORMA, OBJETIVA-SE AVALIAR AS PROPRIEDADES MECâNICAS EM TRAçãO E FLEXãO DE COMPóSITOS DE MATRIZ POLIMéRICA COM ADIçãO EM PERCENTUAL DE CARGA DE LAMA VERMELHA. OS COMPóSITOS FORAM FABRICADOS MANUALMENTE, SEGUINDO AS NORMAS ASTM D638-2014 PARA TESTES DE RESISTêNCIA à TRAçãO E ASTM D790-2017 PARA FLEXãO. OS RESULTADOS APONTAM QUE O AUMENTO EM PERCENTUAL DE LAMA VERMELHA ATUOU COMO CARGA, NãO MELHORANDO SIGNIFICATIVAMENTE AS RESISTêNCIA A FLEXãO E A TRAçãO. A ANOVA CONFIRMOU QUE HOUVE DIFERENçAS SIGNIFICATIVAS ENTRE OS RESULTADOS APRESENTADOS E, PELO TESTE DE TUKEY, FOI POSSíVEL CONFIRMAR QUE A DIFERENçA PERCENTUAL DE CARGA APRESENTOU EFEITO NO TRATAMENTO. SENDO ASSIM, A UTILIZAçãO DE RESíDUO DE LAMA VERMELHA CONSTITUI-SE COMO UMA MATéRIA-PRIMA INFLUENTE NO DESENVOLVIMENTO DE MATERIAIS COMPóSITOS

THE DEVELOPMENT OF NEW MATERIALS THAT USE RAW MATERIALS FROM INDUSTRIAL WASTE IS DESIRABLE FOR APPLICATIONS IN SEVERAL INDUSTRIAL AREAS, AIMING AT THE OPTIMIZATION AND BETTER USE OF THESE INPUTS. RED MUD, WHICH COMES FROM THE ALUMINUM PRODUCTION PROCESS, IS AN ABUNDANT INDUSTRIAL WASTE AND IS RARELY USED FOR REUSE OR REPURPOSING. THUS, THE OBJECTIVE OF THIS STUDY IS TO EVALUATE THE MECHANICAL PROPERTIES IN TENSION AND FLEXURE OF POLYMER MATRIX COMPOSITES WITH A PERCENTAGE ADDITION OF RED MUD LOAD. THE COMPOSITES WERE MANUFACTURED MANUALLY, FOLLOWING THE ASTM D638-2014 STANDARDS FOR TENSILE STRENGTH TESTS AND ASTM D790-2017 FOR FLEXURE. THE RESULTS INDICATE THAT THE INCREASE IN THE PERCENTAGE OF RED MUD ACTED AS A LOAD, WITHOUT SIGNIFICANTLY IMPROVING THE FLEXURAL AND TENSILE STRENGTHS. ANOVA CONFIRMED THAT THERE WERE SIGNIFICANT DIFFERENCES BETWEEN THE RESULTS PRESENTED AND, THROUGH THE TUKEY TEST, IT WAS POSSIBLE TO CONFIRM THAT THE PERCENTAGE DIFFERENCE IN LOAD HAD AN EFFECT ON THE TREATMENT. THEREFORE, THE USE OF RED MUD RESIDUE CONSTITUTES AN INFLUENTIAL RAW MATERIAL IN THE DEVELOPMENT OF COMPOSITE MATERIALS.

Keywords

Lama vermelha; caracterização mecânica, Compósitos

Red mud; mechanical characterization, Composites