Title

DETERMINAÇÃO DE PROPRIEDADES À FLEXÃO EM COMPÓSITOS EPÓXI DE MÉDIA E ALTA FRAÇÕES VOLUMÉTRICAS TEÓRICAS DE TECIDO DE RAMI PARA ANÁLISE ESTRUTURAL EM TORRES DE AEROGERADORES

DETERMINATION OF FLEXURAL PROPERTIES IN EPOXY COMPOSITES OF MEDIUM AND HIGH THEORETICAL VOLUME FRACTIONS OF RAMIE WOVEN FABRIC FOR STRUCTURAL ANALYSIS IN WIND TURBINE TOWERS

Authorship

MACHADO, MARCELO VITOR FERREIRA; LOPES, FELIPE PERISSÉ DUARTE; SIMONASSI, NOAN TONINI; MONTEIRO, SERGIO NEVES

MACHADO, MARCELO VITOR FERREIRA

3 Articles, Downloaded 6 Times

LOPES, FELIPE PERISSÉ DUARTE

I am this author

SIMONASSI, NOAN TONINI

I am this author

MONTEIRO, SERGIO NEVES

I am this author

DOI

10.5151/2594-5327-40507

Downloads

Abstract

A CARACTERIZAçãO MECâNICA DE COMPóSITOS DE MATRIZ EPóXI REFORçADOS COM MéDIA E ALTA FRAçõES VOLUMéTRICAS DE TECIDO DE RAMI POR ENSAIOS DE FLEXãO DE TRêS PONTOS é O OBJETIVO DESTE TRABALHO. A PARTIR DOS TESTES, OS MóDULOS DE ELASTICIDADE, TENSõES LIMITES DE PROPORCIONALIDADE E RESISTêNCIA SãO OBTIDAS, ASSIM COMO, AS RESISTêNCIAS ESPECíFICAS à FLEXãO. FORAM UTILIZADAS TANTO AMOSTRAS íNTEGRAS QUANTO CORPOS DE PROVA ENVELHECIDOS DE FORMA ACELERADA POR AçãO DE RAIOS ULTRAVIOLETA E CONDENSAçãO. EVIDENTEMENTE, PODE SER NOTADA SIGNIFICATIVA DEGRADAçãO DE PROPRIEDADES MECâNICAS NO MATERIAL EXPOSTO à SIMULAçãO E, CONSEQUENTEMENTE, HOUVE NECESSIDADE DE INDICAR O USO REVESTIMENTO PROTETOR SOBRE O MATERIAL A FIM DE EVITAR SUA DEGRADAçãO CASO UM PROTóTIPO DE TORRE DE TURBINA EóLICA DE EIXO HORIZONTAL VENHA A SER CONSTRUíDO COM O MESMO. POR FIM, PRIORIZANDO AS MEDIDAS OBTIDAS COM AMOSTRAS íNTEGRAS, ANáLISES INFERENCIAIS REVELARAM CONDIçãO DE IGUALDADE ESTATíSTICA PARA AS MéDIAS DOS MóDULOS DE ELASTICIDADE DAS AMOSTRAS QUE CONTINHAM 40% E 50% DE VOLUME DE REFORçO, ALéM DE DISTINçãO SIGNIFICATIVA ENTRE MéDIAS DE TENSõES MáXIMAS PARA OS CORPOS DE PROVA COM 60% E 50% DE FRAçãO VOLUMéTRICA TEóRICA DE TECIDO DE RAMI

THE MECHANICAL CHARACTERIZATION OF EPOXY MATRIX COMPOSITES REINFORCED WITH MEDIUM AND HIGH VOLUME FRACTIONS OF RAMIE WOVEN FABRIC BY THREE-POINT BENDING TESTS IS THE OBJECTIVE OF THIS STUDY. FROM THE TESTS, THE MODULUS OF ELASTICITY, PROPORTIONAL LIMIT AND FLEXURAL STRENGTH HAVE BEEN DETERMINED, AS WELL AS THE SPECIFIC FLEXURAL STRENGTHS. BOTH INTACT AND AGED SPECIMENS BY SIMULATION OF ULTRAVIOLET RAYS AND CONDENSATION WERE USED. EVIDENTLY, SIGNIFICANT DEGRADATION OF MECHANICAL PROPERTIES COULD BE NOTED IN THE MATERIAL EXPOSED TO THE SIMULATION AND, CONSEQUENTLY, THERE WAS A NEED TO INDICATE THE USE OF A PROTECTIVE COATING ON THE MATERIAL IN ORDER TO AVOID ITS DEGRADATION IF A PROTOTYPE OF A HORIZONTAL AXIS WIND TURBINE TOWER WERE TO BE MANUFACTURED WITH THIS MULTIPHASE MATERIAL. FINALLY, PRIORITIZING THE MEASUREMENTS OBTAINED WITH INTACT SPECIMENS, INFERENTIAL ANALYZES REVEALED A CONDITION OF STATISTICAL EQUALITY FOR THE AVERAGES OF SPECIMEN ELASTIC MODULI FOR THOSE WITH 40% AND 50% REINFORCEMENT VOLUME. THERE WAS A SIGNIFICANT DISTINCTION BETWEEN AVERAGES OF FLEXURAL STRENGTH FOR THE SAMPLES WITH 60% AND 50% THEORETICAL VOLUME FRACTION OF RAMIE WOVEN FABRIC..

Keywords

Compósito Epóxi, Fibras de Rami, Ensaio de flexão, Torres de Aerogeradores

epoxy composite, Ramie fibers, Bending test, Wind Turbines.