DETERMINAÇÃO EXPERIMENTAL DA PROJEÇÃO LIQUIDUS DO SISTEMA NBCRB NA REGIÃO RICA EM NBCR ATÉ 50% AT. B

EXPERIMENTAL EVALUATION OF THE LIQUIDUS PROJECTION IN THE NBCR RICH REGION OF THE NBCRB SYSTEM UNTIL 50% AT. B

Authorship

Gigolotti, João Carlos Jânio; Fiorani, Jean Marc; Coelho, Gilberto Carvalho; David, Nicolas; Nunes, Carlos Angelo

Gigolotti, João Carlos Jânio

I am this author

Fiorani, Jean Marc

I am this author

Coelho, Gilberto Carvalho

I am this author

David, Nicolas

I am this author

Nunes, Carlos Angelo

I am this author

DOI

10.5151/2594-5327-18128

Downloads

Abstract

O avanço tecnológico tem gerado demanda crescente por materiais que possam ser utilizados como substrato/revestimento que possuam uma resistência ótima à oxidação em alta temperatura, o que inclui ligas intermetálicas do sistema (Nb)(FeCrAlYSiB) com estruturas multifásicas. Assim, este trabalho teve por objetivo o estudo experimental da Projeção Liquidus do sistema Nb–Cr–B, na região rica em Nb–Cr até 50% at. de B. Ligas Nb–Cr–B foram produzidas com lingotes de Nb (min. 99,8%), lâminas de Cr (min. 99,996%) e de B (min. 99,5%), em forno a arco sob atmosfera de Argônio. Identificou-se as fases por difração de raios-X, por contraste, em imagens obtidas via microscopia eletrônica de varredura no modo elétrons retro-espalhados, e em microssonda. O estudo determinou as reações de formação das fases NbB2, Nb2B3, Nb3B4, Nb5B6, NbB, Nb3B2, Nbss, Cr2Nb, CrB, Cr5B3, Cr2B, Crss e do líquido L.

The technological advance has generated increasing demand for materials that can be used under high temperature, what includes intermetalilc alloys (Nb)(FeCrAlYSiB) with multiphasic structures, that can also be applied in oxide environments. Thus, this work had for objective the experimentally study of the Liquidus Projection of the Nb–Cr–B system in the Nb–Cr rich region until 50% at. B. Nb–Cr–B alloys had been produced with ingotes of Nb (min. 99.8%) and blades of Cr (min. 99.996%) and B (min. 99.5%), in the voltaic arc furnace under argon atmosphere. The phases had been identified by X-ray diffraction, contrast in backscattered electron imaging mode and microprobe. The study determined the reactions of formation of the phases NbB2, Nb2B3, Nb3B4, Nb5B6, NbB, Nb3B2, Nbss, Cr2Nb, CrB, Cr5B3, Cr2B, Crss and the liquid L.

Keywords

Diagrama de fases; Sistema NbCrB; Projeção Liquidus.

Phase diagram; Nb–Cr–B system; Liquidus projection.