Proceedings of ABM Annual Congress


ISSN 2594-5327

77º Congresso Anual da ABM - Internacional vol. 77, num.77 (2024)


Title

EFEITO DA ADIÇÃO DE SÍLICA NA SINTERIZAÇÃO DA ALUMINA

EFFECT OF ADDING SILICA ON ALUMINA SINTERING

DOI

10.5151/2594-5327-40889

Downloads

Abstract

A INCORPORAçãO DE ADITIVOS DE SINTERIZAçãO NA ALUMINA (AL2O3) TEM O INTUITO DE MELHORAR A EFICIêNCIA NO PROCESSO CERâMICO E, CONSEQUENTEMENTE, NAS PROPRIEDADES FíSICO-QUíMICAS DOS CORPOS CERâMICOS. NESTE TRABALHO, INVESTIGOU-SE A INFLUêNCIA DO ADITIVO SíLICA (SIO2) DURANTE A SINTERIZAçãO DA ALUMINA, UTILIZANDO A CONCENTRAçãO EM PESO DE 2, 4 E 8% PARA A SíLICA EM TRATAMENTO TéRMICO DE SINTERIZAçãO: 1500 °C, TAXA DE 5 ºC/MIN, PATAMAR DE 1 H. AS AMOSTRAS FORAM PREPARADAS POR PRENSAGEM UNIAXIAL A FRIO COM CARGA APLICADA DE 2 TONELADAS. OS CERâMICOS OBTIDOS FORAM SINTERIZADOS E A RETRAçãO LINEAR DOS MESMOS FOI CALCULADA. O ENSAIO DE FLEXãO FOI REALIZADO E OS MóDULOS DE RUPTURA PARA AS CERâMICAS ADITIVADAS COM 2%, 4% E 8% DE SíLICA, FORAM MAIORES COMPARADOS COM A CERâMICA PURA EM 154%, 126% E 51%, RESPECTIVAMENTE, RESULTADO ESTE RATIFICADO PELA ANáLISE ESTATíSTICA. A MORFOLOGIA FINAL FOI OBSERVADA POR MICROSCOPIA ELETRôNICA DE VARREDURA (MEV).

 

THE INCORPORATION OF SINTERING ADDITIVES IN ALUMINA (AL2O3) AIMS TO IMPROVE THE EFFICIENCY OF THE CERAMIC PROCESS AND, CONSEQUENTLY, THE PHYSICAL-CHEMICAL PROPERTIES OF THE CERAMIC SAMPLES. IN THIS WORK, THE INFLUENCE OF THE SILICA ADDITIVE (SIO2) DURING THE SINTERING OF ALUMINA WAS INVESTIGATED, USING WEIGHT CONCENTRATIONS OF 2, 4 AND 8% FOR SILICA IN SINTERING HEAT TREATMENT: 1500 °C, RATE OF 5 ºC/MIN, 1 H THRESHOLD. THE SAMPLES WERE PREPARED BY UNIAXIAL COLD PRESSING WITH AN APPLIED LOAD OF 2 TONS. THE CERAMICS OBTAINED WERE SINTERED AND THEIR LINEAR SHRINKAGE WAS CALCULATED. THE FLEXURAL TEST WAS CARRIED OUT AND THE MODULUS OF RUPTURE FOR THE CERAMICS ADDED WITH 2%, 4% AND 8% SILICA WERE HIGHER COMPARED TO THE PURE CERAMIC AT 154%, 126% AND 51%, RESPECTIVELY, A RESULT RATIFIED BY THE STATISTICAL ANALYSIS. THE FINAL MORPHOLOGY WAS OBSERVED BY SCANNING ELECTRON MICROSCOPY (SEM).

Keywords

Al2O3; SiO2; Sinterização.

Al2O3; SiO2; Sintering.

How to refer

SILVA, DOUGLAS SANTOS; JUNIO, RAÍ FELIPE PEREIRA; NEUBA, LUCAS DE MENDONÇA; MONTEIRO, SERGIO NEVES; SILVA, MARCELO HENRIQUE PRADO DA. EFEITO DA ADIÇÃO DE SÍLICA NA SINTERIZAÇÃO DA ALUMINA , p. 1611-1620. In: 77º Congresso Anual da ABM - Internacional, São Paulo, Brasil, 2024.
ISSN: 2594-5327 , DOI 10.5151/2594-5327-40889