EFEITO DA CONCENTRAÇÃO DE HIDROGÊNIO NAS PROPRIEDADES MECÂNICAS DE UM AÇO AVANÇADO DE ALTA RESISTÊNCIA UTILIZANDO ENSAIOS DE TRAÇÃO DO TIPO BTD

EFFECT OF HYDROGEN CONCENTRATION ON THE MECHANICAL PROPERTIES OF AN ADVANCED HIGH STRENGTH STEEL USING SLOW STRAIN RATE TEST

Authorship

ARRUDA, MARCUS VINICIUS PEREIRA; COSTA, FERNANDO DE SOUZA; PAULA, JULIANA CRISTINA DE; FRANCO, SINÉSIO DOMINGUES; COSTA, FERNANDO DE SOUZA

ARRUDA, MARCUS VINICIUS PEREIRA

I am this author

COSTA, FERNANDO DE SOUZA

I am this author

PAULA, JULIANA CRISTINA DE

I am this author

FRANCO, SINÉSIO DOMINGUES

I am this author

COSTA, FERNANDO DE SOUZA

I am this author

DOI

10.5151/2594-5327-41128

Downloads

Abstract

NESSE ESTUDO FORAM AVALIADAS AMOSTRAS DE UM AHSS (ADVANCED HIGH-STRENGTH STEEL) DE TERCEIRA GERAçãO LAMINADO A FRIO DA CLASSE DE RESISTêNCIA DE 1000 MPA, A PARTIR DE ENSAIOS DE TRAçãO DO TIPO BTD (BAIXA TAXA DE DEFORMAçãO) EM DIFERENTES CONDIçõES DE CARREGAMENTO DE HIDROGêNIO. UTILIZANDO A TéCNICA TDA (THERMAL DESORPTION ANALYSIS), FOI POSSíVEL ESTABELECER DOIS NíVEIS DE HIDROGêNIO DIFUSíVEL NO AçO E AVALIAR O SEU EFEITO SOBRE A DEGRADAçãO DAS PROPRIEDADES MECâNICAS EM TRAçãO COMPARATIVAMENTE COM A CONDIçãO SEM HIDROGêNIO. PARA O MENOR TEOR DE HIDROGêNIO AVALIADO, DA ORDEM DE 0,61 PPM, NãO HOUVE PERDA CONSIDERáVEL DAS PROPRIEDADES MECâNICAS EM RELAçãO à CONDIçãO NãO CARREGADA. CONTUDO, PARA A CONDIçãO DE MAIOR CONCENTRAçãO DE HIDROGêNIO, PRóXIMA DE 1,16 PPM, FOI PERCEBIDA UMA QUEDA SIGNIFICATIVA NOS VALORES DE ALONGAMENTO TOTAL, COM íNDICE DE FRAGILIZAçãO DE 38,3%. A METODOLOGIA APLICADA PERMITIU DISTINGUIR A DEGRADAçãO DAS PROPRIEDADES MECâNICAS EM FUNçãO DA CONCENTRAçãO DE HIDROGêNIO DO MATERIAL, CONSTITUINDO-SE EM UMA IMPORTANTE FERRAMENTA PARA O DESENVOLVIMENTO E A ENGENHARIA DE APLICAçãO DOS AHSS PARA O SETOR AUTOMOTIVO.

IN THIS STUDY, SAMPLES OF A COLD-ROLLED 3RD GENERATION AHSS OF THE 1000 MPA STRENGTH CLASS WERE EVALUATED ON SLOW STRAIN RATE TESTS (SSRT) UNDER DIFFERENT CONDITIONS OF HYDROGEN CHARGING. USING THE THERMAL DESORPTION ANALYSIS (TDA), TWO DIFFUSIBLE HYDROGEN LEVELS WERE OBTAINED IN THE STEEL AND THUS THEIR EFFECT ON THE DEGRADATION OF MECHANICAL PROPERTIES IN TENSION WAS COMPARED TO THE UNCHARGED CONDITION. FOR THE LOWEST HYDROGEN CONTENT EVALUATED, OF THE ORDER OF 0.61 PPM, THERE WAS NO CONSIDERABLE LOSS OF MECHANICAL PROPERTIES IN RELATION TO THE UNCHARGED CONDITION. HOWEVER, FOR THE HIGHEST HYDROGEN CONCENTRATION, CLOSE TO 1.16 PPM, A SIGNIFICANT DROP IN TOTAL ELONGATION VALUES WAS NOTICED, WITH A CALCULATED EMBRITTLEMENT INDEX OF 38.3%. THE METHODOLOGY APPLIED MADE IT POSSIBLE TO DISTINGUISH THE DEGRADATION OF MECHANICAL PROPERTIES DEPENDING ON THE HYDROGEN CONCENTRATION OF THE MATERIAL, CONSTITUTING AN IMPORTANT TOOL FOR THE DEVELOPMENT AND APPLICATION ENGINEERING OF AHSS FOR THE AUTOMOTIVE SECTOR.