EFEITO DA INCORPORAÇÃO DE CASCA DE CACAU EM PÓ EM UMA MASSA CERÂMICA

EFFECT OF INCORPORATION OF COCOA BARK POWDER INTO A CERAMIC MASS

Authorship

DELAQUA, GEOVANA CARLA GIRONDI; FERREIRA, ELVIS PANTALEÃO; SOUZA, DJALMA; VIEIRA, CARLOS MAURÍCIO FONTES

DELAQUA, GEOVANA CARLA GIRONDI

I am this author

FERREIRA, ELVIS PANTALEÃO

I am this author

SOUZA, DJALMA

I am this author

VIEIRA, CARLOS MAURÍCIO FONTES

I am this author

DOI

10.5151/2594-5327-41332

Downloads

Abstract

O OBJETIVO DESTE TRABALHO FOI A INCORPORAçãO DE CASCA DE CACAU EM MASSA CERâMICA, AVALIANDO A INFLUêNCIA NAS PROPRIEDADES FíSICAS E MECâNICA DAS CERâMICAS. A MATéRIAS-PRIMAS ARGILOSA FOI CARACTERIZADA POR: GRANULOMETRIA, FRX E DRX. FORAM PREPARADAS FORMULAçõES COM DIFERENTES PERCENTUAIS DO RESíDUO, E A PLASTICIDADE FOI AVALIADA. FORAM FEITOS CORPOS DE PROVA POR PRENSAGEM UNIAXIAL, E QUEIMADOS EM DIFERENTES TEMPERATURAS, UTILIZANDO UMA TAXA DE AQUECIMENTO DE 2ºC/MIN E MANTIDOS NA TEMPERATURA DE PATAMAR POR 180MIN. APóS FORAM AVALIADAS AS PROPRIEDADES DE: ABSORçãO DE áGUA E TENSãO DE RUPTURA à FLEXãO POR TRêS PONTOS. COM OS RESULTADOS OBTIDOS OBSERVOU QUE POR SE TRATAR DE UM RESíDUO COM GRANDE QUANTIDADE DE MATéRIA ORGâNICA, A QUANTIDADE DEVE SER AVALIADA PARA NãO PREJUDICAR AS PROPRIEDADES DA CERâMICA. COM ISTO, é POSSíVEL CONCLUIR QUE A INCORPORAçãO DESTE RESíDUO EM CERâMICA é UMA ALTERNATIVA MUITO VANTAJOSA PARA A INDúSTRIA CERâMICA, ONDE OCORRE ECONOMIA DE ENERGIA NO PROCESSO DA QUEIMA

THE OBJECTIVE OF THIS WORK WAS THE INCORPORATION OF COCOA BARK INTO CERAMIC MASS, EVALUATING THE INFLUENCE ON THE PHYSICAL AND MECHANICAL PROPERTIES OF THE CERAMICS. THE CLAYEY RAW MATERIALS WERE CHARACTERIZED BY: GRANULOMETRY, FRX AND DRX. FORMULATIONS WERE PREPARED WITH DIFFERENT PERCENTAGES OF RESIDUE, AND PLASTICITY WAS EVALUATED. SPECIMENS WERE MADE BY UNIAXIAL PRESSING, AND FIRED AT DIFFERENT TEMPERATURES, USING A HEATING RATE OF 2ºC/MIN AND MAINTAINED AT THE PLATEAU TEMPERATURE FOR 180MIN. AFTERWARDS, THE PROPERTIES OF: WATER ABSORPTION AND TENSILE STRENGTH AT THREE-POINT BENDING WERE EVALUATED. WITH THE RESULTS OBTAINED, IT WAS OBSERVED THAT AS IT IS A RESIDUE WITH A LARGE AMOUNT OF ORGANIC MATTER, THE QUANTITY MUST BE EVALUATED SO AS NOT TO HARM THE PROPERTIES OF THE CERAMIC. WITH THIS, IT IS POSSIBLE TO CONCLUDE THAT THE INCORPORATION OF THIS RESIDUE IN CERAMICS IS A VERY ADVANTAGEOUS ALTERNATIVE FOR THE CERAMIC INDUSTRY, WHERE ENERGY SAVINGS OCCUR IN THE FIRING PROCESS

Keywords

Resíduo; Incorporação; Cerâmica Vermelha

Cocoa bark; Red Cerâmic.