EFEITO DA INCORPORAÇÃO DE DIFERENTES TIPOS DE ARGILAS ORGANOFÍLICAS NAS PROPRIEDADES TÊNSEIS DO PET Poli(tereftalato de Etileno)/Argilas Organofílicas

EFFECT OF THE INCORPORATION OF DIFFERENT TYPES OF ORGANOCLAYS ON THE TENSILE PROPERTIES OF PET Poly (ethylene terephthalate)/Organoclay

Authorship

Ferreira, Rodholfo da Silva Barbosa; Andrade, Daniela de Lourdes Anjos Coutinho Simões; Raposo, Claudia Maria de Oliveira; Leite, Itamara Farias; Silva, Suédina Maria de Lima

Ferreira, Rodholfo da Silva Barbosa

I am this author

Andrade, Daniela de Lourdes Anjos Coutinho Simões

I am this author

Raposo, Claudia Maria de Oliveira

I am this author

Leite, Itamara Farias

I am this author

Silva, Suédina Maria de Lima

I am this author

DOI

10.5151/2594-5327-21643

Downloads

Abstract

Visando melhorar as propriedades mecânicas do poli(tereftalato de etileno) (PET) sem modificar as condições de processamento do mesmo, pequeno teor de argila organofílica (1% em massa), preparada com tecnologia nacional, foi incorporada ao PET pelo método de intercalação por fusão para obtenção de nanocompósitos. A morfologia e as propriedades mecânicas (resistência à tração, módulo de Young e alongamento na ruptura) foram investigadas. Os dados de difratometria de raios X evidenciaram que nanocompósitos com morfologia intercalada ordenada e intercalada desordenada foram obtidos, resultando em melhores propriedades tênseis quando comparadas ao do PET puro. Notáveis aumentos na taxa e no grau de cristalização também foram conseguidos com a incorporação das argilas organofílicas ANO19A:F e ANO49A:F ao polímero PET.

In order to improve the tensile properties of poly(ethylene terephthalate) (PET) without modify the processing conditions of the polymer, small content of organoclays (1 wt%), prepared with national technology has been incorporated to PET by melt process. The morphology and mechanical properties (tensile strength, young’s modulus and elongation at break) were investigated. The results of X ray diffraction showed that ordered/disordered intercalated morphology nanocomposites were obtained, resulting in improved tensile properties when compared to pure PET. Remarkable increases in the rate and degree of crystallization were also achieved with the incorporation of ANO19A: ANO49A:F organoclays to polymer PET.

Keywords

Argilas organofílicas; Poli(tereftalato de etileno); Nanocompósitos; Propriedades tênseis.

Organoclays; Poly(ethylene terephthalate); Nanocomposites; Tensile properties.