Title

EFEITO DA MOAGEM DE ALTA ENERGIA (MAE) EM COMPÓSITOS PARTICULADOS DE AÇO EUFORER COM CARBETO DE TÂNTALO (TaC)

EFFECT OF HIGH ENERGY MILLING (MAE) IN PARTICULATE COMPOSITE STEEL WITH EUFORER TANTALUM CARBIDE (TaC)

Authorship

Oliveira, Leiliane Alves de; Gomes,; Umbelino, Uílame; Souza, Calson Pereira; Soares, Sérgio Renato da Silva

Oliveira, Leiliane Alves de

I am this author

Gomes,

I am this author

Umbelino, Uílame

I am this author

Souza, Calson Pereira

I am this author

Soares, Sérgio Renato da Silva

I am this author

DOI

10.5151/2594-5327-23469

Downloads

Abstract

A redução do cavaco do aço ferrítico/martênsítico Eurofer foi promovida durante a moagem de alta energia de misturas de pós de aço EUROFER e TaC nos moinhos planetário e de bolas. A composição empregada possui 3% de TaC em relação a quantidade de pó de aço. Os pós foram processados pela metalurgia do pó através da moagem de alta energia (MAE) por 5 e 8 horas (Planetário) e 24 horas (moinho de bolas). Os produtos das moagens foram caracterizados pelas técnicas de difratometria de raios X, granulometria e microscopia eletrônica de varredura (MEV). Os difratogramas de raios X dos produtos das moagens indicam a presença do TaC e as fases do aço ferrítico/martensítico EUROFER. A granulometria dos compósitos particulados obteve uma grande variação do tamanho das partículas em um gráfico modal com tamanhos médio de partículas de 28,21; 35,06; 20,45 e 24,21m do pó de aço puro com 5hs de moagem, aço com TaC 5h, aço com TaC 8hs e aço com TaC 24hs, respectivamente. As micrografias do MEV apresentam a forma, morfologia e dispersão das partículas dos compósitos particulados.

The reduction of the chip of ferritic steel / martensitic Eurofer was promoted during the high energy milling of powder mixtures of steel EUROFER in TaC and planetary mills and balls. The composition employed has 3% TaC in relation the amount of steel powder. The powders were processed by powder metallurgy by high energy milling (MAE) for 5 to 8 hours (Planetary) and 24 hours (ball mill). The products of the mills were characterized by the techniques of X-ray diffraction, granulometry and scanning electron microscopy (SEM). The X-ray diffractograms of the products of the grinding indicate the presence of TaC and the layers of stainless ferritic / martensitic EUROFER. The particle size of the particulate composites obtained a large variation of particle size on a graph with modal average particle size of 28.21, 35.06, 20.45 and 24.21 m of steel powder with pure 5 h milling , TaC 5h steel, stainless steel and with 8hs TaC TaC with 24 hours, respectively. The SEM micrographs present the shape, morphology and particle dispersion of composite particles.

Keywords

Metalurgia do pó; Aço Eurofer; Carbeto de tântalo; Moagem de alta energia.

Powder metallurgy; Eurofer steel; Tantalum carbide; High-energy milling.