Proceedings of the Seminar on Rolling, Metal Forming and Products


ISSN 2594-5297

Title

EFEITO DA TEMPERATURA DE ACABAMENTO E BOBINAMENTO NA MICROESTRUTURA E NAS PROPRIEDADES MECÂNICAS DE AÇO DE ALTA RESISTÊNCIA COM ESTRUTURA FERRÍTICA BAINÍTICA

EFFECT OF FINISHING DELIVERY TEMPERATURE AND COILING TEMPERATURE ON THE MICROSTRUCTURE AND ON THE MECHANICAL PROPERTIES OF HIGH STRENGTH FERRITE BAINITE STEEL

DOI

10.5151/2594-5297-0082

Downloads

Abstract

O objetivo deste trabalho foi avaliar, em escala industrial, o efeito da temperatura de acabamento (TA) e temperatura de bobinamento (TB) na microestrutura e nas propriedades mecânicas de um aço laminado a quente com estrutura ferrítica bainítica. Constatou-se que, nas faixas avaliadas, o abaixamento da TA e TB resultaram e aumento do limite de resistência devido refinamento de grão e presença de microestruturas aciculares. Tendência de queda do LE foi observada quando TB estava menor que 440oC e TA maior que 860oC, sendo que este fato pode estar associado à geração de discordâncias móveis devido formação das ilhas de bainita/martensita entre a matriz macia de ferrita e/ou devido a precipitação insuficiente de Nb(CN). O alongamento apresentou uma correlação forte com a TB, apresentando uma tendência de queda com o abaixamento deste parâmetro.

 

The aim of this project was to evaluate, with an industrial scale experiment, the effect of finishing delivery temperature (FDT) and coiling temperature (CT) on the microstructure and mechanical properties of a hot rolled ferrite bainite steel. It was observed that the lowering of FDT and CT increases the UTS due the grain refinement and presence of acicular constituents. The YS was diminished when the CT was lower than 440oC and FDT higher than 860oC. This probably is due the formation of martensite/bainite islands within the soft ferrite grains or due the incomplete NbCN precipitation. Elongation has presented a strong relationship with CT, getting lower when this parameter was decreased.

Keywords

Laminação a quente; LTQ; Aços microligados; Aço ferrita bainita.

Hot rolling; Hot strip mill; Micro alloyed steel; Ferrite bainite steel.

How to refer

Barbosa, Gleyson Marcos; Bellon, Júlio Cezar; Guerra, Gladistone de Souza; Santos, Dagoberto Brandão dos. EFEITO DA TEMPERATURA DE ACABAMENTO E BOBINAMENTO NA MICROESTRUTURA E NAS PROPRIEDADES MECÂNICAS DE AÇO DE ALTA RESISTÊNCIA COM ESTRUTURA FERRÍTICA BAINÍTICA , p. 806-812. In: 45º Seminário de Laminação, Processos e Produtos Laminados e Revestidos, Porto de Galinhas - PE, 2008.
ISSN: 2594-5297 , DOI 10.5151/2594-5297-0082