EFEITO DA TEMPERATURA DE QUEIMA NAS PROPRIEDADES MECÂNICAS DA CERÂMICA VERMELHA PARA FABRICAÇÃO DE TELHAS

EFFECT OF FIRING TEMPERATURE ON THE MECHANICAL PROPERTIES OF RED CERAMICS FOR TILES MANUFACTURING

Authorship

PEREIRA, MATHEUS QUEIROZ DE SANT'ANNA; GAMA, FELIPE DAFLON; LIRIO, JOSÉ LUCAS DECOTÉ DE CARVALHO; LINHARES, JOSÉ ALEXANDRE TOSTES; MARVILA, MARKSSUEL TEIXEIRA; VIEIRA, CARLOS MAURÍCIO FONTES

PEREIRA, MATHEUS QUEIROZ DE SANT'ANNA

I am this author

GAMA, FELIPE DAFLON

9 Articles, Downloaded 112 Times

LIRIO, JOSÉ LUCAS DECOTÉ DE CARVALHO

I am this author

LINHARES, JOSÉ ALEXANDRE TOSTES

I am this author

MARVILA, MARKSSUEL TEIXEIRA

I am this author

VIEIRA, CARLOS MAURÍCIO FONTES

I am this author

DOI

10.5151/2594-5327-41557

Downloads

Abstract

ESTE TRABALHO VISA ANALISAR AS CARACTERíSTICAS E PROPRIEDADES TECNOLóGICAS DA ARGILA CINZA, TíPICA DO MUNICíPIO DE CAMPOS DOS GOYTACAZES-RJ, VISANDO A FABRICAçãO DE TELHAS. FOI FEITO UM ENSAIO DE ESPECTROSCOPIA DE FLUORESCêNCIA DE RAIOS X (FRX) NA MASSA ARGILOSA PARA IDENTIFICARMOS OS CONSTITUINTES DESSA ARGILA. FORAM PREPARADOS CORPOS DE PROVA POR MEIO DE PRENSAGEM UNIAXIAL A 10 TONELADAS, COM QUEIMA EM TEMPERATURAS QUE VARIARAM DE 700°C A 800°C. AS PROPRIEDADES TECNOLóGICAS AVALIADAS APóS A QUEIMA INCLUíRAM RETRAçãO LINEAR, ABSORçãO DE áGUA E RESISTêNCIA à FLEXãO EM TRêS PONTOS E DENSIDADE APARENTE. OS RESULTADOS MOSTRARAM QUE A ARGILA CINZA ORIGINáRIA DE CAMPOS DOS GOYTACAZES-RJ APRESENTOU CARACTERíSTICAS QUE NãO VIABILIZAM SUA UTILIZAçãO PARA TELHAS POIS OBTEVE UMA BAIXA RESISTêNCIA A FLEXãO, NãO ATINGINDO O VALOR EXIGIDO PELA NORMA, E UMA ABSORçãO DE áGUA BEM PRóXIMA DO MáXIMO EXIGIDO PELA NORMA. CONSEQUENTEMENTE NOS INDICANDO A DIFíCIL APLICABILIDADE DESSE TIPO DE ARGILA PARA PRODUçãO DE TELHAS, PORéM SE ENQUADRANDO NAS NORMAS DE PRODUçãO DE TIJOLOS, COMO é COMUMENTE UTILIZADA NA REGIãO.

THIS WORK AIMS TO ANALYZE THE CHARACTERISTICS AND TECHNOLOGICAL PROPERTIES OF GRAY CLAY, TYPICAL OF THE MUNICIPALITY OF CAMPOS DOS GOYTACAZES-RJ, AIMING TO MANUFACTURE TILES. AN X-RAY FLUORESCENCE SPECTROSCOPY (XRF) TEST WAS CARRIED OUT ON THE CLAY MASS TO IDENTIFY THE CONSTITUENTS OF THIS CLAY. SPECIMENS WERE PREPARED USING UNIAXIAL PRESSING AT 10 TONS, WITH FIRING AT TEMPERATURES RANGING FROM 700°C TO 800°C. THE TECHNOLOGICAL PROPERTIES EVALUATED AFTER FIRING INCLUDED LINEAR SHRINKAGE, WATER ABSORPTION AND THREE-POINT FLEXURAL STRENGTH AND APPARENT DENSITY. THE RESULTS SHOWED THAT THE GRAY CLAY ORIGINATING FROM CAMPOS DOS GOYTACAZES-RJ PRESENTED CHARACTERISTICS THAT DO NOT ALLOW ITS USE FOR TILES AS IT HAD A LOW FLEXURAL RESISTANCE, NOT REACHING THE VALUE REQUIRED BY THE STANDARD, AND A WATER ABSORPTION VERY CLOSE TO THE MAXIMUM REQUIRED BY THE STANDARD. CONSEQUENTLY, INDICATING THE DIFFICULT APPLICABILITY OF THIS TYPE OF CLAY FOR THE PRODUCTION OF TILES, HOWEVER, IT FITS WITHIN THE STANDARDS FOR BRICK PRODUCTION, AS IS COMMONLY USED IN THE REGION.

Keywords

Argila; Cerâmica Vermelha; Telha; Temperatura

Clay; Red Ceramics; Roof Tile; Temperature.