Abstract

A produção de componentes com aços microligados pela técnica de forjamento exige tratamentos térmicos para obtenção das propriedades especificadas pelas normas. Associadas à fabricação dos produtos forjados, a adição de nióbio é um fator importante como refinador de grão, modificador da microestrutura e propriedades mecânicas do aço. Considerando os efeitos do nióbio e as temperaturas de tratamento térmico o objetivo desta pesquisa foi a fabricação de barras forjadas de um aço microligado com nióbio com secção quadrada de 40 mm. Estas barras foram recozidas a 930 °C e submetidas aos tratamentos de têmpera a 855, 900 e 1000 °C. O modelo de Kasatkin foi utilizado para selecionar as temperaturas de aquecimento no interior, próxima e acima da região intercrítica do aço. Após o resfriamento em água, as microestruturas do aço foram observadas e correlacionadas às medidas de dureza. Os resultados comprovam a validade do modelo de Kasatkin e o efeito do nióbio no tamanho de grão e na microestrutura do aço microligado forjado.

 

The production of microalloyed steels components by the forging technique requires heat treatments to obtain the properties specified by the standards. Associated with the manufacture of forged products, the niobium addition is an important factor as a grain refining, modifier of the microstructure and mechanical properties of the steel. Considering the niobium effects and the heat treatment temperatures the objective of this research was the manufacture of a microalloyed steel containing niobium forged bars with a square section of 40 mm. These bars were annealed at 930 °C and subjected to quenching at 855, 900 and 1000 °C. The Kasatkin model was used to choose the temperature in the interior, near and above the intercritical region of the steel. After cooling in water, the microstructures of the steel were observed and correlated to the hardness measurements. The results confirm the validity of the Kasatkin model and the the niobium effect on grain size and microstructure of the forged microalloyed steel.

Keywords

Aço forjado; Aço microligado com nióbio; Modelo de Kasatkin.

Forged steel; Kasatkin model; Microalloyed steel containing niobium.