EFEITO DA VARIAÇÃO DOS PARÂMETROS DE SOLDAGEM SOBRE AS PROPRIEDADES DE REVESTIMENTOS DE AÇO INOXIDÁVEIS APLICADOS PELOS PROCESSOS SAW E FCAW

EFFECT OF THE VARIATION OF WELDING PARAMETERS ON THE PROPERTIES OF STAINLESS STEEL OVERLAYS APPLIED BY FCAW AND SAW PROCESS

Authorship

Melo, Raphael Henrique Falcão de; Pontes, Mariana Karla Gurjão; Nóbrega, Jailson Alves da; Maciel, Theophilo Moura; Santos, Marco Antonio dos

Melo, Raphael Henrique Falcão de

I am this author

Pontes, Mariana Karla Gurjão

I am this author

Nóbrega, Jailson Alves da

I am this author

Maciel, Theophilo Moura

I am this author

Santos, Marco Antonio dos

I am this author

DOI

10.5151/2594-5327-21165

Downloads

Abstract

O objetivo deste trabalho foi avaliar a influência da variação dos parâmetros de soldagem sobre as características de cordões de solda de aço inoxidável depositados em chapas do aço A36 pelos processos SAW e FCAW. Para isto, utilizou-se a técnica do planejamento experimental fatorial em dois níveis, tendo como fatores de controle a tensão de referência, a velocidade de alimentação do arame e a velocidade de soldagem. Determinando-se a influência deste sobre os valores de diluição, microdureza e microestrutura em diferentes regiões dos cordões de solda. A diluição a variou de 11,61% a 27,01% no processo SAW e de 9,23% a 14,28% no processo FCAW, enquanto que a microestrutura resultante apresentou uma matriz austenítica com ferrita rendilhada e ferrita AF para ambos os processos. Os valores médios de microdureza Vickers foram de 211,2 HV para o processo SAW e 191,6 HV para o FCAW.

The aim of this study was to evaluate the influence of the variation of welding parameters on the characteristics of weld beads of stainless steel deposited on plates of A36 steel by SAW and FCAW processes. For this purpose, it was used the technique of design of experiments in two levels, with voltage, wire feed rate and travel speed as control factors. Being determined the influence of this on dilution, hardness and microstructure in different regions of the weld beads. The dilution ranged from 11.61% to 27.01% in the SAW process, and from 9.23% to 14.28% in the FCAW process, while the microstructure has an austenitic matrix with lacy ferrite and ferrite AF for both processes. The average values of hardness Vickers were of 211.2 HV for the SAW process and 191.6 HV for the FCAW process.

Keywords

Revestimentos; Aço inoxidável; Microestrutura; Processos SAW e FCAW.

Weld overlays; Stainless steel; Microstructure; SAW and FCAW processes.