EFEITO DO PONTO DE ORVALHO DA ATMOSFERA DOS FORNOS DE RECOZIMENTO CONTÍNUO NA QUALIDADE DO REVESTIMENTO GA EM AÇO DUAL PHASE

EFFECT OF DEW POINT OF ATMOSPHERE OF CONTINUOUS ANNEALING FURNACES ON THE QUALITY OF GA COATING ON DUAL PHASE STEEL

DOI

10.5151/2594-5297-24095

Downloads

Abstract

A condição superficial do aço após a etapa de recozimento da CGL é de extrema importância para a qualidade do revestimento galvannealed (GA). A presença de óxidos ou precipitados pode afetar as reações na interface revestimento/substrato e diminuir a molhabilidade do Zn na superfície do aço. Visando evitar a oxidação do material durante o recozimento, emprega-se uma atmosfera protetora nos fornos de recozimento. Mas, apesar dessa atmosfera, é possível a ocorrência de oxidação seletiva ou de precipitação de partículas de segunda fase na superfície do aço, sendo o ponto de orvalho (PO) empregado um dos fatores preponderantes no sentido de se obter a condição superficial mais favorável à galvanização a quente. Neste estudo avaliou-se o efeito do PO sobre a qualidade de revestimento GA aplicado em aço dual phase. Em um Simulador do Processo de Galvanização a Quente (HDPS) realizou-se o recozimento contínuo utilizando desde atmosferas mais secas (PO = -60°C) até mais úmidas (PO = 0°C), assim como a galvanização a quente. Concluiu-se que o PO é determinante para a quantidade, distribuição e tipo de óxidos formados, sendo as condições de -60°C a -30°C as que proporcionaram a obtenção dos revestimentos com melhor qualidade superficial e maior aderência.

 

The steel surface condition after continuous annealing of strip is extremely important to the quality of galvannealed coating (GA). The presence of oxides or precipitates can affect the reactions at the coating/substrate interface and decrease the zinc wettability on the steel surface. To avoid oxidation of the material during continuous annealing, a protective atmosphere is used in the furnaces. Despite this atmosphere, it is possible the selective oxidation or precipitation of second phase particles, being the dew point of atmosphere one of the leading factors in order to obtain the most favorable surface condition to hot dip galvanizing. This study aimed to evaluate the effect of the dew point on the quality of GA coatings applied to dual phase steel. The continuous annealing under atmospheres with dew points from -60°C to 0°C, as well as hot dip galvanizing, were performed in a Hot Dip Process Simulator (HDPS). It was found that the dew point has a decisive influence on the amount, distribution and type of oxides formed, and the conditions from -60°C to -30°C provided the coatings with improved surface quality and better adhesion.

Keywords

Recozimento contínuo; Ponto de orvalho; Aço dual phase; Revestimento GA.

Continuous annealing; Dew point; Dual phase steel; GA coating.

How to refer

Guimarães, Juliana Porto; Barbosa, Aldo Henrique de Almeida; Gonzalez, Berenice Mendonça; Vieira, Ronaldo Rodrigues. EFEITO DO PONTO DE ORVALHO DA ATMOSFERA DOS FORNOS DE RECOZIMENTO CONTÍNUO NA QUALIDADE DO REVESTIMENTO GA EM AÇO DUAL PHASE , p. 877-888. In: 50º Seminário de Laminação, São Paulo, 2013.