Proceedings of ABM Annual Congress


ISSN 2594-5327

62º Congresso anual da ABM vol. 62, num.62 (2007)


Title

EFEITO DO PRÉ-AQUECIMENTO E DO TRATAMENTO TÉRMICO DE ALÍVIO DE TENSÕES NA MICROESTRUTURA E DUREZA DE SOLDAS DE PONTEAMENTO EM AÇO ASTM A516 GRAU 70

THE EFFECT OF PREHEATING AND STRESS RELIEVE HEAT TREATMENT IN MICROSTRUCTURE AND HARDNESS OF TACK WELDS IN ASTM A516 GRADE 70 STEEL

DOI

10.5151/2594-5327-0423

Downloads

Abstract

Na fabricação por soldagem é comum a utilização de dispositivos auxiliares de montagem ponteadas diretamente na peça a ser fabricada. Este trabalho tem como objetivo estudar alterações metalúrgicas ocorridas devido à técnica de ponteamento com o processo de soldagem MIG-MAG em chapas de aço ASTM A516 grau 70 com espessura de 31,5 mm. Amostras foram preparadas utilizando pré-aquecimento à temperatura ambiente, 120°C e 180°C, que foram analisadas na condição como soldada e após tratamento térmico de alívio de tensões (TTAT) por técnicas de microscopia ótica e dureza. Os resultados mostram que, na condição como soldada, as soldas de ponteamento necessitam ser pré-aquecidas ao menos a 120oC a fim de obter dureza adequada do metal de solda e na zona termicamente afetada (ZTA) do metal base. Por outro lado, após TTAT, mesmo as soldas de ponteamento sem pré-aquecimento apresentaram valores de dureza adequados. Conclui-se que o procedimento de soldagem para ponteamento do aço ASTM A516 grau 70 deve ser realizado com pré-aquecimento mínimo de 120oC caso o equipamento não seja submetido a TTAT após a soldagem, mas este pré-aquecimento pode ser dispensado caso o equipamento sofra TTAT após a soldagem.

 

In the fabrication by welding is common the use of auxiliary set-up devices tacked directly at the work piece to be produced. The purpose of this work is to study the metallurgical changes that happen due to the technique of tack weld with the MIG-MAG process in ASTM A516 grade 70 plate of 31,5 mm thick. Samples were prepared using preheat at the room temperature, 120°C and 180°C, which were analyzed at the as-welded condition and after the stress relieving heat treatment (SRHT) by means of optical microscopy and hardness techniques. The results have shown that, at the as-welded condition, the tack welds must be preheated at least at 120°C in order to obtain appropriate hardness of the fusion zone (FZ)l and the heat affected zone (HAZ) of the base metal. On other hand, after SRHT, even the tack welds without preheating presented appropriate values of hardness. It can be concluded that the welding procedure for the tack welds of the ASTM A516 grade 70 steel must be made with the minimum preheating temperature of 120°C if the equipment will not be submitted to SRHT after welding, but tack weld preheating may be suppressed if the equipment undergoes PWHT after welding.

Keywords

Ponteamento; Pré-aquecimento; Tratamento térmico de alívio de tensões; Dureza; Microestrutura.

Tack weld; Preheating; Stress relieving heat treatment; Hardness; Microstructure.

How to refer

Côrtes, José Renato Azevedo; Tatagiba, Luiz Cláudio Soares; Paranhos, Ronaldo Pinheiro da Rocha. EFEITO DO PRÉ-AQUECIMENTO E DO TRATAMENTO TÉRMICO DE ALÍVIO DE TENSÕES NA MICROESTRUTURA E DUREZA DE SOLDAS DE PONTEAMENTO EM AÇO ASTM A516 GRAU 70 , p. 3908-3916. In: 62º Congresso anual da ABM, Vitória, 2007.
ISSN: 2594-5327 , DOI 10.5151/2594-5327-0423