EFEITO DO TEMPO ENTRE OS PASSES DO FRICTION STIR PROCESSING (FSP) NA MICROESTRUTURA E NA DUREZA DO ALUMÍNIO 7075-T651

EFFECT OF TIME BETWEEN FRICTION STIR PROCESSING (FSP) PASSES ON THE MICROSTRUCTURE AND HARDNESS OF 7075-T651 ALUMINUM ALLOY

Authorship

DINIZ, SAULO BRINCO; CARIOCA, ROSI HELLEN CALDAS; REIS, LUCAS MOURA MONTENEGRO; MAGALHÃES, HIRON AKIRA YAMADA; CARUNCHIO, ANDRÉ FERRARA; SILVA, CAROLINA PAIVA NASCIMENTO; SILVA, LEONARDO MARTINS DA; MONTEIRO, SERGIO NEVES

DINIZ, SAULO BRINCO

I am this author

CARIOCA, ROSI HELLEN CALDAS

2 Articles, Downloaded 5 Times

REIS, LUCAS MOURA MONTENEGRO

I am this author

MAGALHÃES, HIRON AKIRA YAMADA

I am this author

CARUNCHIO, ANDRÉ FERRARA

I am this author

SILVA, CAROLINA PAIVA NASCIMENTO

I am this author

SILVA, LEONARDO MARTINS DA

I am this author

MONTEIRO, SERGIO NEVES

I am this author

DOI

10.5151/2594-5327-41004

Downloads

Abstract

NOS úLTIMOS ANOS, VáRIOS TRABALHOS VêM SENDO DESENVOLVIDOS NO FRICTION STIR PROCESSING (FSP), CUJOS BUSCAM PRINCIPALMENTE CORRELACIONAR PARâMETROS DE PROCESSO COM MICROESTRUTURAS / PROPRIEDADES OBTIDAS, E DENTRE OS PARâMETROS MENOS ESTUDADOS, SE DESTACA O TEMPO ENTRE OS PASSES. ESTE TRABALHO ESTUDOU AS ALTERAçõES MICROESTRUTURAIS E DE DUREZA PROMOVIDAS PELA VARIAçãO DO TEMPO ENTRE OS PASSES (0 E 5 MINUTOS) AO REALIZAR O FSP EM UMA CHAPA DE ALUMíNIO 7075-T651. PARA TAL, FORAM REALIZADAS ANáLISES VIA MICROSCóPIO ÓPTICO E ELETRôNICO DE VARREDURA, DUREZA SUPERFICIAL ROCKWELL HR30T E DUREZA VICKERS. FOI CONSTATADO QUE A DUREZA TEM UMA TENDêNCIA DE CRESCIMENTO COM A REALIZAçãO DE UM PASSE ADJACENTE, SENDO ESTAS DUREZAS MENORES DO QUE AS DUREZAS DO MATERIAL ANTES DO PROCESSAMENTO. ESTE COMPORTAMENTO ESTA RELACIONADO POSSIVELMENTE DIMINUIçãO DA FRAçãO VOLUMéTRICA DE PRECIPITADOS, PROVENIENTE DO ENGROSSAMENTO

IN RECENT YEARS, SEVERAL WORKS HAVE BEEN DEVELOPED IN FRICTION STIR PROCESSING (FSP), WHICH MAINLY CORRELATE PROCESS PARAMETERS WITH MICROSTRUCTURES / PROPERTIES OBTAINED, AND AMONG THE LEAST STUDIED PARAMETERS, THE TIME BETWEEN PASSES STANDS OUT. THIS WORK STUDY THE CHANGES IN MICROSTRUCTURE AND HARDNESS CAUSED BY VARYING THE TIME BETWEEN PASSES (0 AND 5 MINUTES) WHEN PERFORMING FSP ON A 7075-T651 ALUMINUM ALLOY. FOR THIS PURPOSE, ANALYZES WERE CARRIED OUT BY OPTICAL AND SCANNING ELECTRONIC MICROSCOPE, ROCKWELL HR30T SURFACE HARDNESS AND VICKERS HARDNESS. IT WAS FOUND THAT HARDNESS HAS A TENDENCY TO INCREASE WITH THE COMPLETION OF AN ADJACENT PASS, WITH THESE HARDNESSES BEING LOWER THAN THE HARDNESS OF THE MATERIAL BEFORE PROCESSING. THIS BEHAVIOR IS POSSIBLY RELATED TO THE DECREASE IN THE VOLUMETRIC FRACTION OF PRECIPITATES, RESULTING FROM THICKENING

Keywords

Friction Stir Processing; Al7075-T651; Microestrutura; Dureza.

Friction Stir Processing; Al7075-T651; Microstructure; Hardness.