Title

EFEITO DOS PARÂMETROS DE RECOZIMENTO CONTÍNUO NA MICROESTRUTURA E PROPRIEDADES MECÂNICAS DE UM AÇO REVESTIDO POR IMERSÃO A QUENTE DA CLASSE DE RESISTÊNCIA DE 800 Mpa

EFFECT OF CONTINUOUS ANNEALING PARAMETERS ON MICROSTRUCTURE AND MECHANICAL PROPERTIES OF A HOT DIP GALVANIZED STEEL OF THE 800 MPa STRENGTH CLASS

DOI

10.5151/1983-4764-26169

Downloads

Abstract

Neste trabalho avaliou-se o efeito de diferentes ciclos térmicos na microestrutura e propriedades mecânicas de um aço Dual Phase revestido por imersão a quente, da classe de resistência de 800 MPa, a partir de simulações em escala piloto no equipamento HDPS (Hot Dip Process Simulator), ensaios dilatométricos, tração à temperatura ambiente e flangeamento. Nas simulações de recozimento contínuo foram experimentadas duas temperaturas de encharque no recozimento intercrítico (740°C e 780°C) e três temperaturas de patamar isotérmico no resfriamento rápido (610°C, 560°C e 510°C). A caracterização microestrutural evidenciou que a temperatura de encharque de 740°C não foi suficiente para dissolução completa dos carbonetos formados na laminação a quente, resultando em frações reduzidas de segundo constituinte. Com isso, o limite de resistência mínimo de 800 MPa não foi alcançado. Além disso, os resultados de ductilidade e flangeamento se mostraram aquém dos obtidos nas simulações com encharque a 780°C. Nas simulações com temperatura de encharque a 780°C e isotérmicas de 510°C e 560°C no resfriamento rápido foi atendido o limite de resistência mínimo, com capacidade de expansão de furo ligeiramente superior à obtida nas simulações com encharque a 740°C.

 

In this work was evaluated the effect of different thermal cycles on the microstructures and mechanical properties of a hot dip galvanized Dual Phase steel, class 800 MPa, from simulations in laboratory scale with the equipment HDPS (Hot Dip Process Simulator), dilatometric test, tensile test and flanging test. In the continuous annealing simulations were tested two soaking temperature (740°C and 780°C) and three isothermal temperatures in the rapid cooling (610°C, 560°C and 510°C). Microstructural characterization showed that the soaking temperature at 740°C was not enough for the complete dissolution of carbides, resulting in lower fractions of the second constituent. Thus, the minimum tensile strength was not reached. Furthermore, the ductility and flanging were lower compared to soaking temperature at 780°C. In the thermal cycles at 780°C and isothermal temperature at 510°C and 560°C in the rapid cooling the minimum tensile strength was reached, hole expansion was slightly higher compared to soaking temperature at 740°C.

Keywords

Aços avançados de alta resistência, Dual phase, Recozimento contínuo

Advanced high strength steels, Dual phase, Continuous annealing

How to refer

Guimarães, Gislan William; Cetlin, Paulo Roberto; Rocha, Roberta de Oliveira; Ferreira, Jetson Lemos. EFEITO DOS PARÂMETROS DE RECOZIMENTO CONTÍNUO NA MICROESTRUTURA E PROPRIEDADES MECÂNICAS DE UM AÇO REVESTIDO POR IMERSÃO A QUENTE DA CLASSE DE RESISTÊNCIA DE 800 Mpa , p. 29-38. In: 52º Seminário de Laminação, Rio de Janeiro, 2015.