EFEITOS DA DEFORMAÇÃO PLÁSTICA SEVERA APLICADA A FRIO POR ECAP VIA ROTA C EM UMA LIGA Al AA1070

EFFECTS OF SEVERE PLASTIC DEFORMATION APPLIED THE COLD BY ECAP VIA ROUTE C IN A LEAGUE AL AA1070

Authorship

MENDES, RAQUEL SANTOS; DUARTE, ANA CAROLINA RIBEIRO; LINS, JEFFERSON FABRÍCIO CARDOSO; CASTRO, GABRIEL GONÇALVES PESSOA DE; FONTANA, MANUELA

MENDES, RAQUEL SANTOS

I am this author

DUARTE, ANA CAROLINA RIBEIRO

I am this author

LINS, JEFFERSON FABRÍCIO CARDOSO

I am this author

CASTRO, GABRIEL GONÇALVES PESSOA DE

I am this author

FONTANA, MANUELA

I am this author

DOI

10.5151/1516-392X-26727

Downloads

Abstract

O trabalho teve por objetivo produzir uma liga Al AA1070 com granulometria fina a partir de um material com granulometria grosseira, por meio de deformação plástica severa (DPS) aplicada por prensagem por canais equiangulares (ECAP) via rota C, bem como esclarecer e avaliar os mecanismos responsáveis pela evolução microestrutural durante este processo de prensagem. O processo empregou a rota C com 5 passes consecutivos a frio e acumulou uma deformação ɛ5 = 5,95. O material de partida é proveniente de um processo de laminação a quente, com uma microestrutura de grãos grosseiros com tamanho de grão de 16 ± 18 μm. Foi realizada a caracterização microestrutural com o auxílio das técnicas de microscopia eletrônica de varredura (MEV) e de difração de elétrons retroespalhados. O refinamento microestrutural foi realizado eficientemente alcançando uma microestrutura fina, observou-se uma redução de 80% alcançando um tamanho de grão de 3,38 μm, e um aumento da fração de contornos de alto ângulo passando de 23% a 46%. A partir dos resultados obtidos nas análises conclui-se que os mecanismos responsáveis pela evolução microestrutural foram os processos de subdivisão por meio de fragmentação e rotação de grãos, recuperação e recristalização dinâmica.

The study aimed to produce an alloy Al AA1070 with fine grains from a material with coarse particle size, by DPS applied by ECAP route C, and clarify and assess the mechanisms responsible for the microstructural evolution during this pressing process. Will be held 5 consecutive passes where the deformation accumulated is ɛ5 = 5.95. The starting material is manufactured from a hot-rolling process, and has a coarse grain microstructure with a grain size of 15.7 ± 17.5. Microstructural characterization was performed with the aid of scanning electron microscopy techniques (SEM) and electron backscatter diffraction was performed. The microstructural refinement was carried reaching a fine microstructure, there was a 80% reduction reaching a in achieving a grain size of 3.38 microns, and an increase of the fraction of high angle boundaries from 23% to 46%. From the results obtained in this study it is concluded that the mechanisms responsible for microstructural evolution were the subdivision processes through fragmentation and rotation grains dynamic recovery and recrystallization.

Keywords

Microscopia eletrônica de varredura, Prensagem por canais equiangulares, Liga de alumínio, Deformação plástica severa

Scanning electron microscopy, Pressing by equiangular channels, Aluminum alloy, Severe plastic deformation