ENDURECIMENTO SECUNDÁRIO DO AÇO RÁPIDO AISI M3:2 NOME COMERCIAL SINTER 23 PRODUZIDO POR UMA TÉCNICA DE METALURGIA DO PÓ

SECONDARY HARDENING OF AN AISI M3:2 HIGH SPEED STEEL NAMED SINTER 23 PRODUCED THROUGH POWDER METALLURGY TECHNIQUES

Authorship

Ferreira, Allana Cristina Pires; Santos, Elinaldo Neves dos; Mesquita, Arimatea Pisom de Paiva; Araújo, Edval Gonçalves de; Gonzalez, Cezar Henrique; Ambrozio Filho, Francisco; Araujo Filho, Oscar Olimpio de

Ferreira, Allana Cristina Pires

I am this author

Santos, Elinaldo Neves dos

I am this author

Mesquita, Arimatea Pisom de Paiva

I am this author

Araújo, Edval Gonçalves de

I am this author

Gonzalez, Cezar Henrique

I am this author

Ambrozio Filho, Francisco

I am this author

Araujo Filho, Oscar Olimpio de

I am this author

DOI

10.5151/1516-392X-26915

Downloads

Abstract

O endurecimento secundário de aço rápido AISI M3:2 nome comercial Sinter 23 obtido por uma técnica de metalurgia do pó de sinterização por compactação isostática a quente é objeto desse trabalho de pesquisa. O aço rápido em questão foi austenitizado em banho de sal a 1.140°C, 1.160°C, 1.180°C e 1.200°C, temperado ao ar e revenimento a 540°C, 560°C e 580°C. Amostras do aço rápido foram fabricadas e submetidas ao tratamento térmico acima descrito e submetida a ensaios de dureza Vickers e Rockwell C para a determinação das suas respostas ao tratamento térmico de endurecimento e avaliação do pico de endurecimento secundário através dos resultados de dureza.

The main aim of this work is to study the behaviour of the secondary hardening of AISI M3:2 high speed steel named Sinter 23 obtained by powder metallurgy technique of hot isostatic pressing submitted to a suitable procedure of heat treatment. Sinter 23 was submitted to hardening in order to study the sencondary hardening behaviour of this steel. The M3:2 high speed steel Sinter 23 was submitted to heat treatment of hardening with austenitizing temperatures of 1,140°C, 1,160°C, 1,180°C and 1,200°C and tempering at 540°C, 560°C and finally 580°C. The effectiveness and response of the heat treatment was determined by hardness tests (Vickers and Rockweel C hardness) and had its property of secondary hardness evaluated.