ESQUEMA DE PASSES EM LAMINAÇÃO DE CHAPAS GROSSAS E OTIMIZAÇÃO DA TENACIDADE DO PRODUTO ATRAVÉS DE SIMULAÇÃO VIA EVOLUÇÃO MICROESTRUTURAL

PLATE MILL PASS SCHEDULE AND PRODUCT TOUGHNESS OPTIMIZATION THROUGH MICROSTRUCTURAL EVOLUTION SIMULATION

DOI

10.5151/2594-5297-34829

Downloads

Abstract

A LAMINAÇÃO DE NORMALIZAÇÃO (NR) REQUER UMA FAIXA DE TEMPERATURA DE FINAL DE LAMINAÇÃO ENTRE 860 ° C E 950 ° C, DA MESMA ORDEM DA TEMPERATURA DE AUSTENITIZAÇÃO USADA NO FORNO DE TRATAMENTO TÉRMICO DE NORMALIZAÇÃO. É MUITO COMUM OCORRER RECRISTALIZAÇÃO PARCIAL DA AUSTENITA ENTRE PASSES DE LAMINAÇÃO NESTA FAIXA DE TEMPERATURA DURANTE A LAMINAÇÃO DE NORMALIZAÇÃO DE AÇOS ESTRUTURAIS DE BAIXO CARBONO MICROLIGADOS COM NIÓBIO, SITUAÇÃO EM QUE A TENACIDADE DO PRODUTO PODE SER PREJUDICADA. PORTANTO, É NECESSÁRIO DETERMINAR AS CONDIÇÕES OTIMIZADAS DO PROCESSO NR E SEMPRE CUMPRÍ-LAS. O USO DE FERRAMENTA DE EVOLUÇÃO MICROESTRUTURAL COMO O MICROSIM®, QUE PREVÊ A DISTRIBUIÇÃO DO TAMANHO DO GRÃO DE AUSTENITA AO LONGO DA LAMINAÇÃO A QUENTE, PODE SER EXTREMAMENTE ÚTIL PARA ATINGIR TAL OBJETIVO. ESTE ARTIGO DESCREVE O USO DESSA FERRAMENTA PARA CORRELACIONAR AS CONDIÇÕES DO PROCESSO NR COM A TENACIDADE DA PLACA EM ALGUNS CASOS INDUSTRIAIS. EM UM CASO, AS PREVISÕES DO MICROSIM® FORAM VERIFICADAS COM AS DISTRIBUIÇÕES DE TAMANHO DE GRÃO DETERMINADAS PELA ANÁLISE EBSD. OBTIVERAM-SE RESULTADOS BASTANTE SATISFATÓRIOS, OS QUAIS INDICARAM AS CONDIÇÕES A SEREM SEGUIDAS PARA SE OBTER BONS RESULTADOS DE TENACIDADE EM PLACAS NR DE AÇOS ESTRUTURAIS BAIXO CARBONO MICROLIGADOS COM NIÓBIO.

 

NORMALIZING ROLLING (NR) REQUIRES A FINISHING ROLLING TEMPERATURE RANGE BETWEEN 860°C AND 950°C, OF THE SAME ORDER AS THE AUSTENITIZING TEMPERATURE USED IN THE NORMALIZING HEAT TREATMENT FURNACE. IT IS VERY COMMON TO HAVE PARTIAL AUSTENITE RECRYSTALLIZATION BETWEEN ROLLING PASSES IN THIS TEMPERATURE RANGE DURING THE NORMALIZING ROLLING OF LOW CARBON STRUCTURAL STEELS MICROALLOYED WITH NIOBIUM, A SITUATION WHERE THE TOUGHNESS OF THE PRODUCT CAN BE IMPAIRED. SO, IT IS NECESSARY TO DETERMINE OPTIMIZED NR PROCESS CONDITIONS AND ALWAYS COMPLY WITH THEM. THE USE OF A MICROSTRUCTURAL EVOLUTION TOOL AS MICROSIM®, WHICH PREDICTS THE DISTRIBUTION OF AUSTENITE GRAIN SIZE ALONG HOT ROLLING, CAN BE EXTREMELY USEFUL TO REACH SUCH AIM. THIS PAPER DESCRIBES THE USE OF SUCH TOOL TO CORRELATE NR PROCESS CONDITIONS WITH PLATE TOUGHNESS IN SOME INDUSTRIAL CASES. IN ONE CASE MICROSIM® PREDICTIONS WERE CHECKED WITH GRAIN SIZE DISTRIBUTIONS DETERMINED BY EBSD ANALYSIS. VERY SATISFACTORY RESULTS WERE OBTAINED, WHICH INDICATED SEVERAL RULES TO BE FOLLOWED IN ORDER TO ACHIEVE GOOD TOUGHNESS RESULTS IN NR PLATES OF LOW CARBON STRUCTURAL STEELS MICROALLOYED WITH NIOBIUM.

Keywords

LAMINAÇÃO DE NORMALIZAÇÃO; NIÓBIO; CHAPAS GROSSAS, Evolução microestrutural

Normalizing rolling; Niobium; Plate Mill; Microstructural evolution