ESTUDIO DEL ORIGEN DE INCLUSIONES EN EL REPARTIDOR DE COLADA CONTINUA DE TERNIUM SIDERAR

STUDY ABOUT THE ORIGIN OF INCLUSIONS IN THE TUNDISH OF TERNIUM SIDERAR

DOI

10.5151/2594-5300-17644

Downloads

Abstract

Para la producción de aceros con altas exigencias de calidad es indispensable conocer con precisión las distintas fuentes de generación de inclusiones, de modo de optimizar las prácticas metalúrgicas para minimizar su presencia. El uso de elementos trazadores en la escoria ha mostrado ser una herramienta eficaz para determinar el origen de las inclusiones en los productos de colada continua. En el presente trabajo se realizaron diferentes experiencias utilizando BaCO3 para trazar la escoria de distribuidor. Empleando esta metodología se siguieron diferentes secuencias y se tomaron muestras de planchones en distintos momentos de las coladas. Las muestras fueron exhaustivamente analizadas por medio de microscopía óptica y electrónica de barrido. Se evaluó la densidad, distribución de tamaño y composición de las inclusiones observadas. Los resultados de estos análisis revelaron la presencia de inclusiones con Ba en los planchones cercanos al momento del cambio de cuchara. En cambio, en las muestras correspondientes al período estacionario de la colada no se detectaron este tipo de inclusiones. Las inclusiones con Ba se presentaron con mayor frecuencia en las coladas avanzadas de secuencia y en aquellos casos donde el nivel de distribuidor tuvo un descenso más marcado en el momento del cambio de cuchara. Estos resultados sugieren que la emulsificación producida por el impacto de la corriente de acero líquido al abrir la nueva cuchara puede generar inclusiones que son arrastradas a los moldes. El efecto es más marcado cuando hay una mayor acumulación de escoria en el repartidor. Finalmente, se realizaron también distintas pruebas utilizando elementos modificadores de flujo dentro del distribuidor, analizándose su impacto en la generación y eliminación de las inclusiones.

 

For the production of steels with high quality standards is essential to know accurately the different sources that generate inclusions, in order to optimize the steelmaking practices and to minimize their frequency. The use of tracer elements in the slag has shown an effective tool to determine the origin of inclusions in continuous casting slabs. In the present study different experiences were performed using BaCO3 like a tracer in the tundish slag. Using this methodology slab samples were taken at different times of the castings. The samples were exhaustively analyzed by optical microscopy and SEM/EDS. The density, size distribution and composition of the inclusions observed were evaluated. The results of this analysis revealed the presence of inclusions with Ba in the slab during the transitory state (ladle change). For another hand, samples from the stationary state did not detect this type of inclusions. The Ba inclusions occurred most frequently in advanced casting sequence and in those cases where the tundish level had a weight reduction during the ladle change. These results suggest that the emulsification produced by the impact of the flow of liquid steel can generate inclusions. The effect is more pronounced when there is a greater accumulation of slag in the tundish. Finally, various tests were also performed using flow modifiers within the tundish, analyzing their impact on the generation and elimination of non- metallic inclusions.

Keywords

Inclusiones; Distribuido; Escoria; Trazadores; Transitorios de colado.

Inclusions tracers; Tundish; Slag; Inclusions;Transitory state.