ESTUDO DA FORMAÇÃO E REDUÇÃO DA FERRITA DE ZINCO CONTIDAS NOS PÓS DE ACIARIA ELÉTRICA USANDO MISTURAS CO-CO2

STUDY OF FORMATION AND REDUCTION OF ZINC FERRITE CONTAINED ELECTRIC ARC FURNACE DUSTS BY CO - CO2 GAS MIXTURES

DOI

10.5151/4444-4444-26435

Downloads

Abstract

O presente trabalho trata da formação da ferrita de zinco a partir da mistura e posterior reação solido-solido entre o óxido de zinco e óxido de ferro - Fe2O3 puros em proporções equimolares. A faixa de temperatura onde teve lugar a formação foi entre 1073 e 1373 K. Testes de redução da ferrita de zinco sintética-ZF e pós de aciaria elétrica–EAFD foram realizadas usando misturas de CO e CO2 que variaram entre 50 e 100% CO. Ambos os testes (formação e redução de ZF e EAFD) foram suportados usando técnicas de caracterização física, química, estrutural e microscópica. No caso da redução, foi observado que tanto a temperatura como a percentagem de CO, foram os fatores que, mais afetaram a redução de ferrita de zinco contida no EAFD. A máxima percentagem de redução foi 85%, para 100% CO, 1373 K e 105 min, e 52%, para 50% CO, 1373 K e 105 min. Por outro lado, atingiu o 100% para 100% CO, 1273K, em 80.75 min, 60%, para 50% CO a 1373 K durante 105 min.

 

The present work deals about the zinc ferrite synthesis, occurred through a solidsolid reaction in a selected range of temperatures, using as reactant an equimolar mixture of pure iron oxide- Fe2O3 and pure zinc oxide - ZnO. The range temperature of formation was of 1073 to 1373 K. After that, took place the reduction of equimolar synthetic zinc ferrite-ZF and Electric Arc Furnace Dusts-EAFD by gas mixtures CO - CO2, from 50% and 100% of CO. Both testes (formation and reduction) were supported by physical, chemical, structural and microscopic characterizations of both, initial zinc ferrite generated in laboratory and the remained after reaction. It was observed that the temperature and CO content were the main factors affecting the zinc ferrite reduction. The maximum reductions of ZF indexes obtained in these experiments were 85%, for 100% CO at 1373 K, in 105 min, and 52%, for 50% CO at 1373 K, elapsed 105 min and 100%, for 100% CO at 1273 K, in 80.75 min, and 60%, for 50% CO at 1373K during 105 minutes.

Keywords

Redução, Pós de aciaria elétrica, Ferrita de zinco

Reduction, EAFD, Zinc ferrite

How to refer

Gómez-Marroquín, Mery-Cecilia; D'Abreu, José Carlos; Kohler, Hélio Marques; Rodrigues Filho, Raimundo Nonato. ESTUDO DA FORMAÇÃO E REDUÇÃO DA FERRITA DE ZINCO CONTIDAS NOS PÓS DE ACIARIA ELÉTRICA USANDO MISTURAS CO-CO2 , p. 265-272. In: 45º Ironmaking / 16º Iron Ore / 3º Agglomeration, Rio de Janeiro, 2015.