Title

ESTUDO DA PROPAGAÇÃO DE TRINCAS POR FADIGA EM LIGA TI-52NB PROCESSADA POR FUSÃO EM LEITO DE PÓ A LASER

STUDY OF FATIGUE CRACK GROWTH IN TI-52NB ALLOY PROCESSED BY LASER POWDER BED FUSION

Authorship

SILVA, MATEUS MEDEIROS DA; Morais, Willy Ank de; Landgraf, Fernando José Gomes

SILVA, MATEUS MEDEIROS DA

I am this author

Morais, Willy Ank de

I am this author

Landgraf, Fernando José Gomes

I am this author

DOI

10.5151/2594-4711-40828

Downloads

Abstract

A FUSãO EM LEITO DE Pó A LASER (FLP-L) é UMA TéCNICA DE PRODUçãO DE MATERIAIS DENTRE AS VáRIAS DA MANUFATURA ADITIVA COM GRANDE POTENCIAL DE APLICAçãO NA PRODUçãO DE PRóTESES ORTOPéDICAS DEVIDO AO ELEVADO GRAU DE CUSTOMIZAçãO QUE PERMITE NA PRODUçãO DOS COMPONENTES. CONTUDO, O ESTUDO DO COMPORTAMENTO SOB FADIGA DESTES MATERIAIS é DE GRANDE IMPORTâNCIA PARA SE COMPREENDER COMO ELES PODEM SUBSTITUIR O OSSO HUMANO DA MELHOR FORMA POSSíVEL. ESTE TRABALHO VISA COMPARAR O COMPORTAMENTO DE PROPAGAçãO DE TRINCAS POR FADIGA PARA DOIS MATERIAIS PRODUZIDOS POR FLP-L, UM UTILIZANDO Pó ATOMIZADO A PLASMA (AP) E OUTRO COM Pó HIDROGENADO E DESIDROGENADO (HDH), SEGUNDO A EQUAçãO DE PARIS, DE MODO QUE AS VARIáVEIS DA EQUAçãO FORAM OBTIDAS ANALISANDO-SE A SUPERFíCIE DE FRATURA DE CORPOS DE PROVA PELO MICROSCóPIO ELETRôNICO DE VARREDURA. OS RESULTADOS INDICAM QUE A PROPAGAçãO DE TRINCAS NO MATERIAL PRODUZIDO POR Pó AP OCORRE MAIS FACILMENTE DEVIDO AO SEU MENOR LIMITE DE ESCOAMENTO

LASER POWDER BED FUSION (L-PBF) IS A MATERIAL PRODUCTION TECHNIQUE AMONG THE MANY WITHIN ADDITIVE MANUFACTURING WHICH HAS GREAT POTENTIAL OF APPLICATION IN ORTHOPEDICAL PROTHESIS DUE ITS HIGH DEGREE OF CUSTOMIZATION CONCERNING THE PRODUCTION OF COMPONENTS. HENCE, STUDYING THE FATIGUE BEHAVIOR OF THESE MATERIALS IS SOMETHING OF GREAT IMPORTANCE TO UNDERSTAND HOW THEY CAN SUBSTITUTE THE HUMAN BONE PROPERLY. THIS WORK AIMS TO COMPARE THE FATIGUE CRACK GROWTH BEHAVIOR FOR TWO MATERIALS PRODUCED BY L-PBF, ONE USING PLASMA ATOMIZED (PA) POWDER AND THE OTHER HYDROGENISED-DEHYDROGENISED (HDH) POWDER, ACCORDING TO THE PARIS EQUATION, IN SUCH WAY THAT THE VARIABLES WERE OBTAINED ANALYZING THE FRACTURE SURFACE OF SPECIMENS WITH A SCANNING ELECTRONIC MICROSCOPE. RESULTS SUGGEST CRACK PROPAGATION IN THE MATERIAL PRODUCED BY PA POWDER OCCURS MORE EASILY DUE ITS LESSER YIELD STRENGTH.

Keywords

Propagação de trincas de fadiga; Liga de titânio-nióbio; Fusão em leito de pó a laser

Fatigue crack growth; Titanium-niobium alloy; Laser powder bed fusion