ESTUDO DAS CARACTERÍSTICAS GEOMÉTRICAS E ECONÔMICAS DAS SOLDAS DE REVESTIMENTO PARA OS PROCESSOS MIG E MIG-CW

STUDY OF GEOMETRIC AND ECONOMIC CHARACTERISTCS OF OVERLAY WELDS FOR PROCESSES MIG AND MIG-CW

Authorship

Garcia, Douglas Neves; Mota, Carlos Alberto Mendes da; Mendes, Cássio Patrick Nunes; Assunção, Paulo D’Ângelo; Santo, Henrique Espírito; Rodrigues, Bruno Gonçalves

Garcia, Douglas Neves

I am this author

Mota, Carlos Alberto Mendes da

I am this author

Mendes, Cássio Patrick Nunes

I am this author

Assunção, Paulo D’Ângelo

I am this author

Santo, Henrique Espírito

I am this author

Rodrigues, Bruno Gonçalves

I am this author

DOI

10.5151/2594-5327-16369

Downloads

Abstract

Este trabalho objetiva comparar a características geométricas e econômicas para as soldas de revestimentos dos processos MIG e MIG-CW, com intuito de analisar o ganho de produtividade com a adição do arame frio. As soldas de aço inox foram depositadas pelos processos de soldagem MIG e MIG com adição de arame frio (MIG-CW) na posição plana e sentido de soldagem puxando, modo mecanizado. O metal de base utilizado foi o aço 1020 em chapas com espessura de 6,3 mm. O gás de proteção utilizado foi o Ar-2%O2 a 15 l/min. Depois de realizadas as soldagens, as amostras foram seccionadas e devidamente preparadas através de lixamento e atacadas para análise macrográfica, para a retirada dos valores de largura, reforços e penetração com auxílio de software. Os resultados mostraram um aumento na quantidade em massa de material depositado em função do tempo para o processo MIG-CW sem, contudo afetar a qualidade superficial dos cordões de soldas, além de reduzir a penetração o que é favorável para a soldagem de revestimento em materiais dissimilares, pois diminuirá a diluição.

This paper aims to compare the geometric and economic characteristics for MIG and MIG-CW processes, aiming to analyze the productivity gain with the addition of cold wire. The welding of stainless steel were deposited by the MIG and MIG with addition of cold wire, MIG-CW, processes in the flat position and drawing direction of welding, automated. The base metal used was 1020 steel in plates with a thickness of 6.3 mm. The protection gas used was Ar-2%O2 at 15 L/min. After performed the welding, the samples were selected and properly prepared by sanding and were attacked for macrographs analysis, for the measuring of penetration and reinforcement values were used an aid of software for the calculation of dilution. The results showed an increase in the amount of mass deposited in function of the time for the MIG-CW without affecting the surface quality of the weld, and reduced penetration which is good for overlaying welds in dissimilar materials, because it will decrease the dilution.

Keywords

Soldas de revestimento; Características geométricas e econômicas; Produtividade.

Overlay welds; Geometric and economic characteristics; Productivity.