ESTUDO DAS INCLUSÕES NÃO-METÁLICAS NO PROCESSO DE SOLIDIFICAÇÃO DE UM AÇO API X65 SOUR SERVICE HTP

STUDY OF NON-METALLIC INCLUSIONS IN THE PROCESS OF SOLIDIFICATION OF A STEEL API X65 SOUR SERVICE HTP

Authorship

Escobar, Diana Pérez; Castro, Cynthia Serra Batista; Malynowskyj, Antônio; Camey, Kenji; Taiss, Ed Juarez Mendes; Andrade, Margareth Spangler

Escobar, Diana Pérez

I am this author

Castro, Cynthia Serra Batista

I am this author

Malynowskyj, Antônio

I am this author

Camey, Kenji

I am this author

Taiss, Ed Juarez Mendes

I am this author

Andrade, Margareth Spangler

I am this author

DOI

10.5151/1982-9345-31830

Downloads

Abstract

O presente trabalho estudou a formação de inclusões em um aço HTP (High Temperature Processing) API X65, sour service, submetido ao processo de injeção de Ca e lingotado continuamente com soft reduction dinâmico. Os resultados obtidos na placa foram comparados com uma amostra líquida retirada do distribuidor. A engenharia de inclusões foi respaldada pelo mapeamento com microscópio eletrônico de varredura e metodologia específica. Houve uma diferenciação no nível de limpeza (NL) e tipos de inclusões/partículas entre as amostras, sendo que as relações causa-efeito foram analisadas e discutidas. A maioria das inclusões e partículas detectadas não favorecem trincas induzidas por hidrogênio (HIC).

This paper investigated the formation of inclusions in a steel HTP (High Temperature Processing) API X65, sour service, submitted to the Ca injection process and continuously cast with dynamic soft reduction. The results obtained on the slabs were compared with a liquid sample taken from the tundish. Inclusion engineering was supported by scanning electron microscope mapping and specific methodology. There was a difference in the clean steel level (NL) and types of inclusions / particles between the samples, and the cause-effect relationships were analyzed and discussed. Most inclusions and particles detected do not favor hydrogen-induced cracking (HIC).

Keywords

inclusões não-metálicas; aço HTP; distribuidor; lingotamento contínuo.

non-metallic inclusions; HTP steel; tundish; continuous casting