ESTUDO DAS VARIÁVEIS DE COALESCIMENTO DE NÓDULOS DE FERRO-CARBONO A PARTIR DE MISTURAS E PELOTAS AUTORREDUTORAS NO FORNO ROTATIVO A 1.673 E 1.773 K

STUDY OF COALESCING VARIABLES OF IRON-CARBON NUGGETS FROM MIXTURES AND SELF-REDUCING PELLETS IN THE ROTARY KILN AT 1673 AND 1773 K

Authorship

Nogueira, Alberto Eloy Anduze; Zambrano, Adolfo Pillihuaman; Takano, Cyro; Mourão, Marcelo Breda; Neira, John Bernardo Vilca; ,

Nogueira, Alberto Eloy Anduze

I am this author

Zambrano, Adolfo Pillihuaman

I am this author

Takano, Cyro

I am this author

Mourão, Marcelo Breda

I am this author

Neira, John Bernardo Vilca

I am this author

,

I am this author

DOI

10.5151/2594-357X-17494

Downloads

Abstract

Uma das possibilidades tecnológicas obtidas com a redução de minério de ferro por autorredução é a obtenção de nódulos de ferro-carbono diretamente no processo, como no processo ITmk3. Para compreender melhor o processo de obtenção de nódulos de ferro-carbono no forno rotativo a 1673 e 1773 K, a partir de misturas e pelotas autorredutoras, foi estudado o efeito das seguintes variáveis: temperatura de processamento, temperatura liquidus da escória, quantidade de redutor, e tipo de conformação. Foi empregada uma adaptação do teste de desagregação por tambor (ASTM E279-97) e validado por moagem manual, para medir o grau de coalescimento dos nódulos de ferro-carbono. Como resultados obtiveram-se: O incremento da temperatura de processamento aumenta o processo de coalescimento. A elevada temperatura liquidus da escória, obstaculiza o processo de coalescimento. O incremento da quantidade de redutor acima das necessidades de redução e carburação, restringem o processo de coalescimento. As misturas autorredutoras apresentam um maior grau de coalescimento do que as pelotas autorredutoras

One of the technological possibilities obtained by the reduction of iron ore by self-reduction is to obtain iron-carbon nuggets directly in the process, as in ITmk3 process.To better understand the process of obtain iron-carbon nuggets in a rotary kiln at 1673 and 1773 K from mixtures and self reducing pellets was studied the effect of following parameters: processing temperature, the slag liquidus temperature, the amount of reducer, and the type of conformation. Was used an adaption of the drum test (ASTM E279-97) and validated by manual grinding to measure the degree of coalescence of iron-carbon nuggets. As results were obtained: The increase in processing temperature increases the coalescence process. The high liquidus temperature of the slag, hinder the coalescing process. Increasing the amount of reducer above the needs for reduction and carburization, restrict the coalescence process. Self-reducing mixtures show better degree of coalescence than that of self-reducing pellets.

Keywords

Pelotas autorredutoras; Misturas; Escória; Coalescimento; Nódulos.

Self-reducing pellets; Mixtures; Slag; Coalescence; Nuggets.