ESTUDO DO COMPORTAMENTO ELETROQUÍMICO DE METAIS DUROS DE WC COM LIGANTES À BASE DE COBALTO E NÍQUEL

STUDY OF THE ELECTROCHEMICAL BEHAVIOR OF WC HARD METALS WITH CO AND NI-BASED BINDER

Authorship

CAMPIDELI, VICTOR CARDOSO; SANTOS, JEILCE MARIA ABREU DOS; SILVA, MARIA LAURA NUNES DA; SICUPIRA, DALILA CHAVES; BUENO, GILVANDRO; PENAGOS, JOSE JIMMY

CAMPIDELI, VICTOR CARDOSO

I am this author

SANTOS, JEILCE MARIA ABREU DOS

I am this author

SILVA, MARIA LAURA NUNES DA

I am this author

SICUPIRA, DALILA CHAVES

I am this author

BUENO, GILVANDRO

I am this author

PENAGOS, JOSE JIMMY

I am this author

DOI

10.5151/2594-5327-40748

Downloads

Abstract

A PRENSA DE ROLOS DE ALTA PRESSãO (HPGR) é UTILIZADA NA MINERAçãO PARA A FRAGMENTAçãO DO MINéRIO EM SUBSTITUIçãO AOS MOINHOS DE BOLAS, DEVIDO AO AUMENTO NA CAPACIDADE DA PRODUTIVIDADE DE MOAGEM. PORéM, UMA DESVANTAGEM é O DESGASTE EXCESSIVO DOS PINOS UTILIZADOS NOS REVESTIMENTOS DOS ROLOS QUE, ATUALMENTE, SãO FABRICADOS EM METAL DURO (WC-CO). EM ESTUDOS RECENTES, OS FENôMENOS TRIBOCORROSIVOS SãO CITADOS COMO UM DOS MECANISMOS DE DANIFICAçãO DOS PINOS, SENDO ASSIM, é DE FUNDAMENTAL IMPORTâNCIA AVALIAR A RESISTêNCIA à CORROSãO DOS MESMOS. O PRESENTE ESTUDO VISOU CARACTERIZAR A RESISTêNCIA à CORROSãO DE DIFERENTES METAIS DUROS, VARIANDO O REFINAMENTO DOS GRãOS DE CARBONETO DE TUNGSTêNIO, O TIPO DE LIGANTE (NíQUEL E COBALTO) E A FRAçãO VOLUMéTRICA DOS CONSTITUINTES. O COMPORTAMENTO ELETROQUíMICO DOS MATERIAIS FOI AVALIADO MEDIANTE ENSAIOS DE POLARIZAçãO POTENCIODINâMICA E ESPECTROSCOPIA DE IMPEDâNCIA ELETROQUíMICA EM SOLUçãO DE 3,5% DE NACL. OS ENSAIOS PERMITIRAM AVALIAR A SUSCEPTIBILIDADE à CORROSãO E A TAXA DE CORROSãO DESSES MATERIAIS. AS LIGAS COM MATRIZ DE NíQUEL APRESENTARAM ELEVADA RESISTêNCIA à CORROSãO, POIS ESTE LIGANTE CONTRIBUIU PARA A FORMAçãO DE óXIDOS PROTETORES. DENTRE AS LIGAS COM MATRIZ DE COBALTO, AQUELA COM MENOR FRAçãO VOLUMéTRICA DESTE ELEMENTO E GRãOS MAIS REFINADOS APRESENTOU MAIOR RESISTêNCIA à CORROSãO

HIGH-PRESSURE GRINDING ROLLS (HPGR) IS USED IN MINING FOR ORE FRAGMENTATION AS A REPLACEMENT FOR BALL MILLS, DUE TO THE INCREASED GRINDING PRODUCTIVITY CAPACITY. HOWEVER, ONE DISADVANTAGE IS THE EXCESSIVE WEAR OF THE STUDS USED IN THE ROLL SURFACES, WHICH ARE CURRENTLY MADE OF HARD METAL (WC-CO). RECENT STUDIES HAVE CITED TRIBOCORROSION PHENOMENA AS ONE OF THE MECHANISMS FOR STUD DAMAGE, MAKING IT FUNDAMENTALLY IMPORTANT TO EVALUATE THEIR CORROSION RESISTANCE. THIS STUDY AIMED TO CHARACTERIZE THE CORROSION RESISTANCE OF DIFFERENT HARD METALS, VARYING THE REFINEMENT OF TUNGSTEN CARBIDE GRAINS, THE TYPE OF BINDER (NICKEL AND COBALT), AND THE VOLUMETRIC FRACTION OF THE CONSTITUENTS. THE ELECTROCHEMICAL BEHAVIOR OF THE MATERIALS WAS EVALUATED THROUGH POTENTIODYNAMIC POLARIZATION TESTS AND ELECTROCHEMICAL IMPEDANCE SPECTROSCOPY IN A 3.5% NACL SOLUTION. THE TESTS ALLOWED FOR THE ASSESSMENT OF THE CORROSION SUSCEPTIBILITY AND THE CORROSION RATE OF THESE MATERIALS. THE NICKEL MATRIX ALLOYS SHOWED HIGH CORROSION RESISTANCE, AS THIS BINDER CONTRIBUTED TO THE FORMATION OF PROTECTIVE OXIDES. AMONG THE COBALT MATRIX ALLOYS, THE ONE WITH THE LOWEST VOLUMETRIC FRACTION OF THIS ELEMENT AND THE FINEST GRAINS EXHIBITED THE HIGHEST CORROSION RESISTANCE

Keywords

Metal duro; Corrosão; Tamanho de grãos de WC; Teores de ligantes

Hard metal; Corrosion; WC grain size; Binder contents