ESTUDO DO GRAU DE SENSITIZAÇÃO DO AÇO INOXIDÁVEL UNS S31803 POR ENSAIOS DE REATIVAÇÃO POTENCIODINÂMICA DE DUPLO LOOP

STUDY OF THE DEGREE SENSITIZATION IN UNS S31803 STEEL BY DOUBLE LOOP POTENTIODYNAMIC REACTIVATION TESTS

DOI

10.5151/2594-4711-22855

Downloads

Abstract

O objetivo deste trabalho compreende o estudo do grau de sensitização (GS) do aço UNS S31803 envelhecido a 800ºC por ensaios de reativação potenciodinâmica de duplo loop (DL-EPR). Para isto, corpos de prova do aço em estudo foram solubilizados a 1175ºC e envelhecidos a 800ºC entre 10 min e 72 horas visando a formação de diferentes teores de sigma. Corpos-de-prova metalográficos foram utilizados para a caracterização microestrutural, que foi realizada por meio de técnicas de estereologia quantitativa, análise com ferritoscópio e microscopia eletrônica de varredura (MEV). Os ensaios de DL-EPR foram conduzidos em solução 2M H2SO4 + 0,5M NaCl + 0,01M KSCN à 30ºC, em amostras com acabamento polido. A partir dos ensaios realizados observou-se que o GS das amostras envelhecidas mostra forte dependência da microestrutura. Foi registrada presença de 2 máximos de densidade de corrente na ativação e 2 na reativação, que sugerem a dissolução preferencial de ferrita e austenita. Observa-se ainda aumento do GS até 12 horas de envelhecimento, seguido de queda, indicando a provável redistribuição de Cr para regiões empobrecidas, decorrentes da formação de sigma.

 

The main purpose of this work is the study of the degree sensitization (DOS) of UNS S31803 aged at 800°C by DL-EPR tests. For this, solution heat treatment was conducted at 1175°C for 30 minutes in original samples followed by aging treatment at 800°C between 10 minutes and 72 hours, enabling the formation of different sigma phase contents. The samples aged were mounted in metallography specimens for microstructural characterization that was carried out by quantitative metallography, magnetic measurements and scanning electron microscopy (SEM). The DL-EPR tests were conducted in polished samples at 30°C in a 2M H2SO4 + 0,5M NaCl + 0,01M KSCN solution. A strong relation between the DOS and the microstructure of the samples was observed. It was registered a double maximum current density in activation and in the reactivation suggesting the dissolution of ferrite and austenite phases. It was also registered the DOS increase until 12 hours of aging followed by slight decrease, probably related the Cr redistribution for depleted zones related to sigma formation.

Keywords

Aço inoxidável dúplex; Fase sigma; Grau de sensitização; DL-EPR

Duplex stainless steel; Sigma phase; Degree sensitization; DL - EPR.

How to refer

Morais, Luara da Costa; Santos, Daniella Caluscio dos; Magnabosco, Rodrigo. ESTUDO DO GRAU DE SENSITIZAÇÃO DO AÇO INOXIDÁVEL UNS S31803 POR ENSAIOS DE REATIVAÇÃO POTENCIODINÂMICA DE DUPLO LOOP , p. 1-9. In: 13º ENEMET - Encontro Nacional de Estudantes de Engenharia Metalúrgica, de Materiais e de Minas, São Paulo - Brasil, 2013.