ESTUDO DO MECANISMO DO DEFEITO “COLAMENTO” NO AÇO INOX AISI 304 LAMINADO A FRIO, SEM PRÉVIO RECOZIMENTO

STUD OF THE MECHANISM OF THE DEFECT “COLAMENTO” IN THE AISI 304 STAINLESS STEEL COLD ROLLED, WITHOUT FIRST ANNEALIN

DOI

10.5151/2594-5297-0051

Downloads

Abstract

Na produção de aços Inoxidáveis austeníticos classe ABNT 304, laminados a frio sem recozimento inicial, aparece o defeito denominado “colamento”. O defeito tem como característica a formação de um conjunto disperso de pequenas manchas escuras alongadas na superfície da tira, que se caracteriza por uma diferença de brilho, tornando a superfície mais fosca que a condição normal da Bobina Laminada a Frio – BF e se estende em forma de faixas alongadas no sentido da laminação, Essas manchas foram primeiramente detectadas na linha de inspeção de bobinas laminadas a frio recozidas e decapadas, posteriormente foi constatado que o defeito já existia na Bobina Laminada a frio não recozida. A pesquisa mostrou que, o não fechamento por deformação a frio, das cavidades nos contornos de grão, provocadas pela corrosão intergranular da decapagem química de HF/HNO3, em aços com teores mais elevados de carbono e sensitizados, constitui o mecanismo de formação do defeito “colamento”. As principais variáveis de processo que levam ao aparecimento do defeito são: A corrosão intergranular pela decapagem como o HF-HNO3, associado a temperatura de bobinamento acima de 610°C e o teor de carbono do aço, acima de 0,050% C. O plano de passes da laminação a frio deve ser ajustado, com menores reduções nos primeiros passes, para absorver um produto de maior resistência mecânica.

 

In the production of austenitic stainless steels class AISI 304 cold rolled without first annealing, the defect called "colamento” appears. The defect has is characterized by the formation of a dispersed group of small stringiest dark stains in the surface of the strip, that it is characterized by a difference of shine, turning the dullest surface than the normal condition of the Cold Rolled Coil – BF, and it extends as prolonged band in the rolling direction. Those stains were detected firstly in the inspection line of the cold annealed and picked strips, later on it was verified that the defect already existed in the cold rolled coil before annealing. The research showed that, the non-closing grain boundaries cavities by cold deformation, caused by intergranular corrosion by HF/HNO3 pickling in steels with high content of carbon and sensitized constitute the mechanism of formation of the defect " colamento ".The main process variables that are responsible for the occurrence of this defect are: the coiling temperature above 610°C and the raised carbon content of the steel above 0,050% C. The cold rolling pass schedule was adjusted, with small reductions in the first passes, in order to absorb a product of larger mechanical strengths.

Keywords

Colamento; Aço inox ABNT 304

Stainless steel ABNT 304.

How to refer

Campos, Adão Adélcio; Cunha, Cleber Barros; Rossi, Edson Hugo; Castro, Geovane Martins; Batista, José Carlos; Ferreira, José Sergio. ESTUDO DO MECANISMO DO DEFEITO “COLAMENTO” NO AÇO INOX AISI 304 LAMINADO A FRIO, SEM PRÉVIO RECOZIMENTO , p. 454-463. In: 43º Seminário de Laminação, Processos e Produtos Laminados e Revestidos, São Paulo, 2006.
ISSN: 2594-5297 , DOI 10.5151/2594-5297-0051