ESTUDO E CARACTERIZAÇÃO DE SÓIS DE PSEUDOBOEMITA FIBRILAR OBTIDOS EM DIFERENTES TEMPOS DE ENVELHECIMENTO TÉRMICO

STUDY AND CHARACTERIZATION OF THE SUNS PSEUDOBOEHMITE OBTAINED AT DIFFERENT TIMES OF THERMAL AGING

Authorship

Rocha, Gisele de Araujo; Coelho, Antonio Carlos Vieira; Santos, Pérsio de Souza

Rocha, Gisele de Araujo

I am this author

Coelho, Antonio Carlos Vieira

I am this author

Santos, Pérsio de Souza

I am this author

DOI

10.5151/2594-5327-17875

Downloads

Abstract

O monohidróxido de alumínio boemita, quer bem cristalizado, quer pseudoboemita, é precursor de aluminas de transição que são utilizadas comumente como catalisadores e adsorventes. A síntese foi realizada a partir de um alcóxido de alumínio em solução ácida à 88 ̊C. Pós de pseudoboemita fibrilar foram obtidos por esse mesmo método de preparação, porém os sóis aquosos foram envelhecidos em diferentes tempos: 24, 48 e 168 horas. Essas três dispersões aquosas (sóis) foram secas ao ar, à temperatura ambiente, como membranas. O material foi caracterizado por Espectroscopia no Infravermelho com Transformada de Fourier (FTIR) por meio de técnicas de transmissão como complementação às Difrações de Raios-X (DRX) anteriormente realizadas. Os espectros e difratogramas são apresentados nesse trabalho. Nesse estudo percebe-se que a média do comprimento das fibrilas varia de acordo com a amostra, e os tamanhos aumentam com o tempo de envelhecimento térmico.

The monohydroxy aluminum boehmite, well crystallized or pseudoboehmite, is a precursor of transition aluminas that are commonly used as catalysts and adsorbents. The synthesis was performed from an aluminum alkoxide in acid solution at 88 ̊C. Fibrillar pseudoboehmite powders were obtained by that method of preparation, however the aqueous sols were aged at different times: 24, 48 and 168 hours. These three aqueous dispersions (sols) were dried in air at room temperature, such as membranes. The material was characterized by Infrared Fourier Transform Spectroscopy (FTIR) through transmission techniques as a complement to X-Ray Diffraction (XRD) carried out previously. The spectra and XRD patterns are presented in this work. In this study it is observed that the average length of the fibrils varies according to sample sizes and increases with thermal aging time.

Keywords

Pseudoboemita; Fibrilar; Espectroscopia no infravermelho com tansformada de Fourier; Difração de Raio X.

Pseudoboehmite; Fibrillar; Infrared Fourier transform spectroscopy; X- ray diffraction.