ESTUDO EXPERIMENTAL DA MORFOLOGIA E ESTEREOLOGIA DE CARACTERÍSTICOS EM UMA MICROESTRUTURA MODELO

EXPERIMENTAL STUDY OF MORPHOLOGY AND STEREOLOGY IN THE CHARACTERISTICS IN A MODEL MICROSTRUCTURAL

Authorship

Cardoso, Álan; Dutra, Júlio César

DOI

10.5151/2594-5327-16294

Downloads

heading.download_article_detail 48 Downloads

Abstract

Este trabalho tem como objetivo demonstrar experimentalmente a validade dos modelos matemáticos de morfologia e de estereologia quantitativa utilizados na caracterização das microestruturas dos materiais. Diversas esferas coloridas de massa plástica foram produzidas manualmente e suas medidas de diâmetro foram tomadas. Em seguida, as esferas foram colocadas sobre uma placa de acrílico com o maior empacotamento bidimensional possível. Outra placa de acrílico foi colocada na superfície exposta destas esferas e o conjunto foi comprimido de modo a provocar o preenchimento de espaço entre as esferas. As regras morfológicas foram observadas e comparadas com aquelas descritas por Smith (1951). Também foi possível a medida do número médio de lados das figuras formadas, que é seis. Verificou-se, portanto, que as esferas organizadas, quando expostas em um espaço bidimensional, tendem a respeitar as regras morfológicas como a forma e o número médio de lados do grão. Foi possível ainda relacionar as medidas estereológicas de fração de pontos (PP) e fração em área (AA) com a fração volumétrica (VV), o volume médio e o tamanho médio do característico (no caso, esferas de massa plástica de diferentes cores).

 

This paper aims to demonstrate experimentally the validity of mathematical models of morphology and quantitative stereology used in the characterization of microstructures of materials. Different coloured spheres of plastic mass were manually produced and their diameters were taken. They were then placed on an acrylic plate with the highest possible two-dimensional packing. Another plate was placed on the exposed surface of these spheres and they were compressed so as to fill in the spaces between the spheres. The morphological rules were observed and compared with those described by Smith (1951). It was also possible to measure the average number of sides of the figures formed, which is six. Therefore, arranged balls, when exposed in a two-dimensional space, tend to respect the rules in form and the average number of sides. It was possible to relate the stereological measurements, the point fraction (Pp) and area fraction (AA) to volume fraction (Vv), the average volume, and the average size of the feature (in this case, spheres of plastic mass of different colours).

Keywords

Estereologia; Caracterização microestrutural; Morfologia.

Stereology; Microstructural characterization; Morphology.