ESTUDO EXPLORATÓRIO DE LIGAS MULTICOMPONENTES À BASE DE NICRFECOTI E NICRFECOTINB PARA APLICAÇÃO EM AMBIENTES CORROSIVOS

EXPLORATORY STUDY OF MULTICOMPONENT ALLOYS BASED ON NICRFECOTI AND NICRFECOTINB FOR APPLICATION IN CORROSIVE ENVIRONMENTS

Authorship

RIBEIRO, RAFAELLA MARTINS; BARREIRO, ANNA CAROLINA FIGUEIREDO CARVALHO

RIBEIRO, RAFAELLA MARTINS

I am this author

BARREIRO, ANNA CAROLINA FIGUEIREDO CARVALHO

I am this author

DOI

10.5151/2594-5327-41435

Downloads

Abstract

COM A NECESSIDADE DE APRIMORAMENTO DE PROPRIEDADES COMO RESISTêNCIA à CORROSãO E RESISTêNCIA à ALTAS TEMPERATURAS, UMA NOVA ABORDAGEM VEM SENDO APLICADA PARA O DESENVOLVIMENTO DE LIGAS METáLICAS. POR MEIO DA UTILIZAçãO DE CINCO OU MAIS COMPONENTES PRINCIPAIS, EM QUANTIDADE APROXIMADAMENTE EQUIATôMICAS, ESTAS LIGAS MULTICOMPONENTES PODEM APRESENTAR MICROESTRUTURAS FINAIS ESPECIAIS E, CONSEQUENTEMENTE, PROPRIEDADES INTERESSANTES. O PRESENTE TRABALHO APRESENTA UM ESTUDO EXPLORATóRIO DE DIFERENTES E INéDITAS COMPOSIçõES QUíMICAS MULTICOMPONENTES LEVANTADAS COM BASE NAS PROPRIEDADES INDIVIDUAIS DE CADA ELEMENTO, OBJETIVANDO-SE OBTER UMA LIGA FINAL RESISTENTE à CORROSãO, COMO AS SUPERLIGAS DE NíQUEL. UTILIZANDO-SE O MéTODO CALPHAD (SIMULAçãO TERMODINâMICA), FOI ANALISADO E DISCUTIDO O MIX MICROESTRUTURAL OBTIDO PARA 14 COMPOSIçõES DE LIGAS A BASE DE NICRFECOTI COM A ADIçãO DE DIFERENTES ELEMENTOS DE LIGA, DE MANEIRA A SE AVALIAR A LIGA COM MAIOR POTENCIALIDADE DE APLICAçãO PARA ESTUDOS FUTUROS. DE TODAS AS COMPOSIçõES ANALISADAS, A LIGA NICR0,25FE1,25CO1,25TI1,25 FOI CONSIDERADA A MAIS PROMISSORA POR MAXIMIZAR A FORMAçãO DE SOLUçõES SóLIDAS DE INTERESSE

WITH THE NEED TO ENHANCE PROPERTIES SUCH AS CORROSION RESISTANCE AND HIGH-TEMPERATURE RESISTANCE, A NEW APPROACH HAS BEEN APPLIED TO THE DEVELOPMENT OF METALLIC ALLOYS. BY UTILIZING FIVE OR MORE PRINCIPAL COMPONENTS IN APPROXIMATELY EQUIATOMIC AMOUNTS, THESE MULTICOMPONENT ALLOYS CAN EXHIBIT UNIQUE FINAL MICROSTRUCTURES AND, CONSEQUENTLY, INTERESTING PROPERTIES. THIS WORK PRESENTS AN EXPLORATORY STUDY OF DIFFERENT AND UNPRECEDENTED MULTICOMPONENT CHEMICAL COMPOSITIONS BASED ON THE INDIVIDUAL PROPERTIES OF EACH ELEMENT, AIMING TO OBTAIN A FINAL ALLOY WITH CORROSION RESISTANCE SIMILAR TO THAT OF NICKEL-BASED SUPERALLOYS. USING THE CALPHAD METHOD (THERMODYNAMIC SIMULATION), THE MICROSTRUCTURAL MIX OBTAINED FOR 14 NICRFECOTI-BASED ALLOY COMPOSITIONS WITH THE ADDITION OF DIFFERENT ALLOYING ELEMENTS WAS ANALYZED AND DISCUSSED TO EVALUATE THE ALLOY WITH THE HIGHEST POTENTIAL FOR FUTURE STUDIES. AMONG ALL THE ANALYZED COMPOSITIONS, THE NICR0,25FE1,25CO1,25TI1,25 ALLOY WAS CONSIDERED THE MOST PROMISING DUE TO ITS MAXIMIZATION OF THE FORMATION OF SOLID SOLUTIONS OF INTEREST

Keywords

Ligas de Alta Entropia; Ligas multicomponentes; CALPHAD

High entropy alloys; multicomponent alloys; CALPHAD.