ESTUDO MICROESTRUTURAL DA ESCÓRIA DE CONVERTEDOR LD E SUA RELAÇÃO COM O PROCESSO DE DESFOSFORAÇÃO

MICROSTRUCTURAL STUDY OF THE LD CONVERTER SLAG AND ITS RELATIONSHIP TO THE DEPHOSPHORISATION PROCESS

DOI

10.5151/2594-5300-22815

Downloads

Abstract

A escória de convertedor LD desempenha papel fundamental no refino do aço, principalmente na remoção do fósforo. Muito se sabe sobre as características físico- químicas da escória e sua relação com a eficiência do processo de refino, porém poucos utilizam o aspecto microestrutural para tal análise. Neste sentido, este trabalho teve como objetivo analisar a microestrutura da escória formada nos convertedores da Usiminas e compreender aspectos importantes relacionados à reação de desfosforação, para atuar de maneira efetiva na melhoria do processo industrial. Foi verificado que a reação de desfosforação não ocorre junto às fases sólidas da escória. De acordo com estas observações, a quantidade de fundentes adicionada ao convertedor foi revista, alcançando-se uma expressiva redução no teor de CaO livre das escórias. Foi possível observar, também, uma redução de 10% no consumo de cal carregado nos convertedores, sem interferir no teor médio de fósforo do aço ao fim de sopro.

 

The LD converter slag plays an important role in the refining process, mainly in relationship to phosphorus removal. Much is known about the physicochemical characteristics of the slag and its relationship to the process efficiency. However, few employ the microstructural aspect for such analysis. In this sense, the aim of this work was to analyze the converter slag microstructure and its relationship to dephosphorisation reaction, to act efficiently in the industrial process improvement. It was verified that dephosphorisation reaction does not occur in solid state. According to this observation, the amount of fluxes added to the converter was reviewed, reaching a considerable reduction in the free CaO content of the slags. It was also observed a drop of approximately 10% in lime charged to the converters, without interfere in the mean phosphorus content at the end of oxygen blown.

Keywords

Escória de convertedor; CaO livre; Microestrutura; Desfosforação.

Converter slag; Free CaO; Microstructure; Dephosphorization.