ESTUDO MORFOLÓGICO DE VARIAÇÃO TÉRMICA DE ARMAGASSA GEOPOLIMÉRICA REFORÇADA COM ESCÓRIA DE ALTO FORNO (EAF)

MORPHOLOGICAL STUDY OF THERMAL VARIATION OF GEOPOLYMERIC MORTAR REINFORCED WITH BLAST FURNACE SLAG

Authorship

FERREIRA, PAULO ANDERSON ARANHA; NASCIMENTO, DAMARES DA CRUZ BARBOSA; CORRÊA, THIAGO; MONTEIRO, SÉRGIO NEVES; CANDIDO, VERÔNICA SCARPINI; SILVA, ALISSON CLAY RIOS DA

FERREIRA, PAULO ANDERSON ARANHA

I am this author

NASCIMENTO, DAMARES DA CRUZ BARBOSA

I am this author

CORRÊA, THIAGO

I am this author

MONTEIRO, SÉRGIO NEVES

I am this author

CANDIDO, VERÔNICA SCARPINI

I am this author

SILVA, ALISSON CLAY RIOS DA

I am this author

DOI

10.5151/2594-5327-40464

Downloads

Abstract

OS GEOPOLíMEROS SãO MATERIAIS INORGâNICOS, ALUMINOSILICATOS ATIVADOS ALCALINAMENTE POR REAçãO DE GEOPOLIMERIZAçãO. POR APRESENTAREM PROPRIEDADES SEMELHANTES AO CIMENTO PORTLAND, PESQUISAS VêM SENDO REALIZADAS PARA GARANTIR O USO DE GEOPOLíMEROS NA CONSTRUçãO CIVIL. DESSA FORMA, O PRESENTE TRABALHO ABORDA A PRODUçãO DE ARGAMASSAS GEOPOLIMéRICAS, ADICIONADAS DE ESCóRIA DE ALTO FORNO (EAF), SUBMETIDAS A UMA TEMPERATURA DE 300°C E 800°C. PARA ESTE ESTUDO, FORAM UTILIZADOS METACAULIM, ESCóRIA DE ALTO FORNO (EAF), E AREIA COMERCIAL EM QUANTIDADE DE 0%, 59%, 69% E 75%, E PARA SOLUçãO ALCALINA FORAM ESCOLHIDOS O HIDRóXIDO DE POTáSSIO (KOH) E O SILICATO DE SóDIO (NA2SIO3). APóS PRODUçãO, FORAM CURADOS E LOGO SUBMETIDOS A UMA TEMPERATURA DE 300°C E 800°C. PARA FINS DE ANáLISE, FORAM REALIZADAS CARACTERIZAçõES DE MICROSCOPIA ÓPTICA (MO) E REFINAMENTO DE RIETVELD DA MATéRIA-PRIMA. POR FIM, OS RESULTADOS APONTAM A ARGAMASSA GEOPOLíMERICA COM 69% DE AGREGADO COMO UM MATERIAL SUPERIOR AS OUTRAS FORMULAçõES, EM RAZãO DO BAIXO PERCENTUAL DE DEFEITOS NA MORFOLOGIA DA SUPERFíCIE FRAGMENTADA, CONSIDERANDO A VARIAçãO DE TEMPERATURA, DE 300°C A 800°C.

GEOPOLYMERS ARE INORGANIC MATERIALS, ALUMINOSILICATES ACTIVATED ALKALINE BY GEOPOLYMERIZATION REACTION. BECAUSE THEY HAVE PROPERTIES SIMILAR TO PORTLAND CEMENT, RESEARCH HAS BEEN CARRIED OUT TO ENSURE THE USE OF GEOPOLYMERS IN CIVIL CONSTRUCTION. THUS, THE PRESENT WORK APPROACHES THE PRODUCTION OF GEOPOLYMERIC MORTARS, ADDED WITH BLAST FURNACE SLAG (BFS), SUBMITTED TO A TEMPERATURE OF 300°C AND 800°C. FOR THIS STUDY, METAKAOLIN, BLAST FURNACE SLAG (BFS), AND COMMERCIAL SAND IN AMOUNTS OF 0%, 59%, 69% AND 75% WERE USED, AND FOR ALKALINE SOLUTION POTASSIUM HYDROXIDE (KOH) AND SILICATE WERE CHOSEN OF SODIUM (NA2SIO3). AFTER PRODUCTION, THEY WERE CURED AND THEN SUBJECTED TO A TEMPERATURE OF 300°C AND 800°C. FOR ANALYSIS PURPOSES, OPTICAL MICROSCOPY (OM) AND RIETVELD REFINEMENT CHARACTERIZATIONS OF THE RAW MATERIAL WERE PERFORMED. FINALLY, THE RESULTS POINT TO GEOPOLYMER MORTAR WITH 69% AGGREGATE AS A MATERIAL SUPERIOR TO OTHER FORMULATIONS, DUE TO THE LOW PERCENTAGE OF DEFECTS IN THE MORPHOLOGY OF THE FRAGMENTED SURFACE, CONSIDERING THE TEMPERATURE VARIATION, FROM 300°C TO 800°C.

Keywords

geopolímeros; argamassa; morfologia

Geopolymers; Mortar; Morphology.