ESTUDO POST MORTEM PARA DETERMINAÇÃO DOS MECANISMOS DE DESGASTE DO CADINHO DO ALTO FORNO #2 DA CSN

POST MORTEM STUDY TO DETERMINE THE WEAR MECHANISMS OF CSN # 2 BLAST FURNACE HEARTH REFRACTORY LINING

DOI

10.5151/2594-357X-20568

Downloads

Abstract

Em 2009 foi realizado um reparo parcial no Alto Forno #2 da CSN. Durante o reparo parcial foram retiradas amostragem dos blocos de carbono do cadinho com o objetivo de realizar estudo post mortem visando identificar os mecanismos de desgaste. No estudo post mortem foi realizada a caracterização físico-química das amostras dos blocos de carbono do cadinho, a qual compreendeu as seguintes técnicas: análise química por fluorescência de raios X (FRX), análise de fases mineralógicas por difratometria de raios X (DRX), determinação massa especifica real por picnometria de hélio, análise microestrutural por microscopia eletrônica de varredura (MEV) e mapeamento elementar por energia dispersiva de raios X (EDS). O estudo revelou que os blocos de carbono, mesmo após 26 Mt de gusa produzidos, preservam as suas características físico-químicas na região oposta aos furos de gusa. No entanto, os blocos de carbono da região ao redor dos furos de gusa, apresentaram infiltrações de gusa e de escória e uma acentuada deposição de zinco.

 

In 2009 was realized one partial repair in CSN #2 Blast Furnace. In this partial repair, samples was collected of the carbon based refractory lining with the goal to develop “post mortem” studies for determine the main mechanisms of corrosion, In this “post mortem” study was realized physical-chemical characterization of the samples collected of refractory lining, by the follow technical’s: chemical analyses by X ray fluorescence (XRF), mineralogical phases analysis by X ray diffraction (XRD), real density by helium picnometry, microstructures analysis by scanning electron microscopy (SEM/EDS). The study showed that carbon based refractory, even after 26Mt hot metal produced, keep with the same physical-chemical characteristics in region opposite of iron notch. However, the based carbon brick’s near around the iron notch, appears infiltration of hot metal and slag and a considerable deposition of zinc.

Keywords

Alto forno; Cadinho; Post mortem; Refratário

Blast furnace; Hearth; Post mortem; Refractory.

How to refer

Júnior, Fernando Vernilli; Silva, Sidiney Nascimento; Neves, Elton Silva; Junior, Alecir Lopes Saraiva; Almeida, Bruno Vidal de. ESTUDO POST MORTEM PARA DETERMINAÇÃO DOS MECANISMOS DE DESGASTE DO CADINHO DO ALTO FORNO #2 DA CSN , p. 983-993. In: 41º Ironmaking and Raw Materials Seminar and 12º Brazilian Symposium on Iron Ore, Vila Velha, 2011.