Title

ESTUDO SOBRE A ADIÇÃO DE NB E N AO AÇO AISI 310

A STUDY ON NB AND N ADDITION TO AISI 310 STEEL

Authorship

BRASILEIRO, MARIA LUIZA WEDDERHOFF; GARCIA, JULIANNA MAGALHAES; NUNES, THAISSA SAMPAIO; SOUSA, TALITA GAMA DE; BRANDÃO, LUIZ PAULO MENDONÇA

BRASILEIRO, MARIA LUIZA WEDDERHOFF

I am this author

GARCIA, JULIANNA MAGALHAES

I am this author

NUNES, THAISSA SAMPAIO

I am this author

SOUSA, TALITA GAMA DE

I am this author

BRANDÃO, LUIZ PAULO MENDONÇA

I am this author

DOI

10.5151/2594-5327-40900

Downloads

Abstract

O DESENVOLVIMENTO DE NOVAS LIGAS METáLICAS ESTá AMPLAMENTE LIGADO à ADIçãO DE NOVOS ELEMENTOS DE LIGA EM AçOS CONHECIDOS, COMO é O CASO DO AçO AISI 310 COM ADIçãO DE NITROGêNIO E NIóBIO. O PRESENTE ESTUDO TEVE ENFOQUE EM COMPARAR OS RESULTADOS DE TESTES DE TRAçãO, MICRODUREZA VICKERS E DUREZA HRB DE AMOSTRAS DO NOVO AçO 310 NBN AOS RESULTADOS DOS TESTES REALIZADOS EM CORPOS DE PROVA NO AçO 310 ATUALMENTE EMPREGADO NA INDúSTRIA. A PARTIR DISSO, FOI POSSíVEL COMPREENDER A MUDANçA DAS PROPRIEDADES COM A ADIçãO DOS ELEMENTOS DE LIGA, ASSIM COMO O MECANISMO DE FRATURA QUE OCORRE EM CADA CASO. A ANáLISE MICROESTRUTURAL DA FRATURA DOS ENSAIOS DE TRAçãO FOI ATRAVéS DE ENSAIOS DE MICROSCOPIA ELETRôNICA DE VARREDURA. FOI VERIFICADO QUE HOUVE AUMENTO CONSIDERáVEL DA DUREZA E DA RESISTêNCIA, MANTENDO UMA BOA DUCTILIDADE NO METAL.

THE DEVELOPMENT OF NEW METALLIC ALLOYS IS CLOSELY TIED TO THE INTRODUCTION OF ADDITIONAL ALLOYING ELEMENTS TO EXISTING STEELS. THIS STUDY FOCUSES ON AISI 310 STEEL, SPECIFICALLY WITH THE INCORPORATION OF NITROGEN AND NIOBIUM, RESULTING IN A NOVEL ALLOY REFERRED TO AS 310 NBN STEEL. THE RESEARCH AIMED TO COMPARE THE MECHANICAL PROPERTIES OF THE NEW 310 NBN STEEL WITH THOSE OF THE CONVENTIONAL 310 STEEL USED IN INDUSTRY. TENSILE TESTS, VICKERS MICROHARDNESS, AND HRB HARDNESS TESTS WERE CONDUCTED ON SAMPLES OF BOTH STEEL TYPES. THE RESULTS PROVIDED INSIGHT INTO THE CHANGES IN PROPERTIES DUE TO THE ADDITION OF NITROGEN AND NIOBIUM, AS WELL AS THE FRACTURE MECHANISMS INVOLVED. MICROSTRUCTURAL ANALYSIS OF THE TENSILE TEST FRACTURES WAS PERFORMED USING SCANNING ELECTRON MICROSCOPY. THE FINDINGS REVEALED A SIGNIFICANT INCREASE IN HARDNESS AND STRENGTH IN THE 310 NBN STEEL, WHILE MAINTAINING GOOD DUCTILITY.

Keywords

AISI 310; Nióbio; Nitrogênio; Fratura.

AISI 310; Niobium; Nitrogen; Fracture.