Title

EVOLUÇÃO MICROESTRUTURAL E COMPORTAMENTO MECÂNICO DO AÇO EUTETÓIDE SUBMETIDO A FORJAMENTO MULTIDIRECIONAL COM BAIXA AMPLITUDE DE DEFORMAÇÃO

MICROSTRUCTURAL EVOLUTION AND MECHANICAL BEHAVIOR OF EUTECTOID STEEL SUBJECTED TO MULTIDERECTIONAL FORGING WITH LOW STRAIN AMPLITUDE

Authorship

DOI

10.5151/2594-5327-42256

Downloads

0 Downloads

Abstract

Este trabalho investigou a evolução microestrutural e comportamento mecânico do aço eutetóide SAE 1080 processado por Forjamento Multidirecional (MDF) com baixa amplitude de deformação (∆ε ≈ 0,075) à temperatura ambiente até uma deformação acumulada de 5,4. A caracterização microestrutural, realizada por microscopia eletrônica de varredura, revelou progressivo curvamento e fragmentação parcial das lamelas de cementita. Embora tenha sido observada redução inicial do espaçamento interlamelar (Sp), valores superiores à condição inicial foram registrados em deformações mais elevadas, configurando morfologia microestrutural distinta daquela promovida por processos monotônicos como trefilação e HPT. A análise do comportamento mecânico evidenciou curva de fluxo com aspecto semelhante ao observado em processos de recuperação dinâmica. Observou-se aumento do limite de escoamento e da microdureza Vickers com o avanço da deformação, com aparente estabilização para altas deformações acumuladas. Os resultados evidenciam o impacto da trajetória de deformação na evolução microestrutural e resistência mecânica de aços perlíticos processados por MDF de baixa amplitude.

 

THIS STUDY INVESTIGATED THE MICROSTRUCTURAL EVOLUTION AND MECHANICAL BEHAVIOR OF EUTECTOID SAE 1080 STEEL PROCESSED BY MULTI-DIRECTIONAL FORGING (MDF) WITH LOW STRAIN AMPLITUDE (∆ε ≈ 0.075) AT ROOM TEMPERATURE, REACHING ACCUMULATED STRAINS UP TO ε ≈ 5.4. MICROSTRUCTURAL CHARACTERIZATION, PERFORMED BY SCANNING ELECTRON MICROSCOPY, REVEALED PROGRESSIVE BENDING AND PARTIAL FRAGMENTATION OF CEMENTITE LAMELLAE. ALTHOUGH AN INITIAL REDUCTION IN INTERLAMELLAR SPACING (SP) WAS OBSERVED, HIGHER VALUES THAN THE AS-RECEIVED CONDITION WERE REGISTERED AT HIGHER STRAINS, LEADING TO A DISTINCT MICROSTRUCTURAL MORPHOLOGY COMPARED TO THAT TYPICALLY PROMOTED BY MONOTONIC PROCESSES SUCH AS WIRE DRAWING AND HPT. THE ANALYSIS OF MECHANICAL BEHAVIOR SHOWED A FLOW CURVE RESEMBLING THAT TYPICALLY OBSERVED IN DYNAMIC RECOVERY PROCESSES. AN INCREASE IN YIELD STRENGTH AND VICKERS MICROHARDNESS WAS OBSERVED WITH INCREASING STRAIN, FOLLOWED BY AN APPARENT STABILIZATION AT HIGHER ACCUMULATED STRAINS. THE RESULTS HIGHLIGHT THE INFLUENCE OF THE DEFORMATION PATH ON THE MICROSTRUCTURAL EVOLUTION AND MECHANICAL STRENGTH OF PEARLITIC STEELS PROCESSED BY MDF WITH LOW STRAIN AMPLITUDE

Keywords

Deformação Plástica Severa, Forjamento multidirecional, Aço Eutetóide, Microestrutura, Caminho de De

How to cite

TELES, JULIANA MARIA SILVA; BARTULICI, ERIC; BORGES, ALEX RODRIGUES; CETLIN, PAULO ROBERTO; FLAUSINO, PAULA CIBELY ALVES; MANHABOSCO, TAISE MATTE; SILVA, NAYARA APARECIDA NERES DA. EVOLUÇÃO MICROESTRUTURAL E COMPORTAMENTO MECÂNICO DO AÇO EUTETÓIDE SUBMETIDO A FORJAMENTO MULTIDIRECIONAL COM BAIXA AMPLITUDE DE DEFORMAÇÃO, p. 1272-1284. In: 78th ABM Annual Congress - International, São Paulo, Brasil, 2025.