Proceedings of the Seminar on Rolling, Metal Forming and Products


ISSN 2594-5297

Title

EVOLUÇÃO MICROESTRUTURAL DE AÇO DA CLASSE DE 700 MPa NA LAMINAÇÃO DE TIRAS A QUENTE

MICROSTRUCTURE EVOLUTION OF 700 MPa HOT ROLLED STEEL STRIP

DOI

10.5151/1983-4764-31814

Downloads

Abstract

Aços laminados a quente para aplicação estrutural na indústria automotiva com limite de escoamento (LE) mínimo de 700 MPa são normalmente microligados ao Nb e Ti, endurecidos por precipitação de TiC. Nesse trabalho foi avaliada a evolução da microestrutura e os efeitos da escala de passes e da temperatura de bobinamento, via simulação laboratorial por ensaios de torção e análises por EBSD, na microestrutura final e na dureza desse aço. Foi mostrado que, para as composições de liga analisadas, a alteração da escala de passes pouco afeta a microestrutura final. No entanto, a temperatura de bobinamento (TB) tem efeito marcante na microestrutura e no LE. Aumentando a TB de 550°C até 620°C, o LE obtido na simulação do processo industrial diminuiu, o que poderia ser devido à queda da contribuição da precipitação de TiC ao endurecimento. Porém, foi mostrado que o aço bobinado a 550°C possuía elevado potencial de precipitação adicional, especialmente em temperaturas na faixa de 600°C a 650°C, abrindo possibilidades para aumento do LE.

 

Hot rolled steels for structural application in the automotive industry having minimum yield stress (YS) of 700 MPa are usually microalloyed with Nb andTi, strengthened by TiC precipitation. This paper shows the microstructure evolution and the effects of pass schedule and coiling temperature on final microstructure and hardness, using hot torsion simulation and EBSD analyses. In the steels studied changing the pass schedule has negligible effect on final microstructure. However, the coiling temperature (CT) exerts marked influence on both microstructure and YS. By the increase of CT from 550°C to 620°C in the torsion simulations, there was a decrease in YS, that would be attributed to reducing precipitation effect of TiC. However, it was shown that the steel coiled at 550°C had a great potential for additional precipitation, especially between 600°C and 650°C, giving rise to YS improvement.

Keywords

Tiras a Quente; Evolução microestrutural; Aço 700 MPa

Hot strip; Microstructure evolution; 700 MPa steel

How to refer

Santos, Antonio Adel dos; Murari, Fabio Dian; Avelar Junior, Ailton Ribeiro de; Pereda, Beatriz; Soria Beatriz Lopez. EVOLUÇÃO MICROESTRUTURAL DE AÇO DA CLASSE DE 700 MPa NA LAMINAÇÃO DE TIRAS A QUENTE , p. 379-390. In: 55º Seminário de Laminação e Conformação, São Paulo, 2018.
ISSN: 2594-5297 , DOI 10.5151/1983-4764-31814