FORMULAÇÃO DE BARBOTINA PARA A OBTENÇÃO DE PEÇAS CERÂMICAS PEQUENAS COM ESPESSURA DE PAREDES REDUZIDA

SLIP FORMULATION FOR OBTAINING SMALL CERAMIC PARTS WITH REDUCED WALL THICKNESS

Authorship

NASCIMENTO, DAMARES DA CRUZ BARBOSA; ROSA, DIEMISON LIRA SANTA; SOARES, EDSON MIRANDA; NASCIMENTO, GABRIELLA DA SILVA; ALMEIDA, OLÍVIA LOPES LEITE; HILDEBRANDO, EDEMARINO ARAUJO

NASCIMENTO, DAMARES DA CRUZ BARBOSA

I am this author

ROSA, DIEMISON LIRA SANTA

I am this author

SOARES, EDSON MIRANDA

I am this author

NASCIMENTO, GABRIELLA DA SILVA

I am this author

ALMEIDA, OLÍVIA LOPES LEITE

I am this author

HILDEBRANDO, EDEMARINO ARAUJO

I am this author

DOI

10.5151/2594-5327-41228

Downloads

Abstract

BARBOTINA é UM PROCESSO BASTANTE INFLUENTE PARA A ATIVIDADE DE CONFORMAçãO CERâMICA E, é UTILIZADA LARGAMENTE NA INDúSTRIA CERâMICA PARA PRODUZIR MATERIAIS PELO MéTODO DE COLAGEM. ESSE PROCESSO CONSISTE NA REMOçãO DA PARTE LíQUIDA DE UMA SUSPENSãO COLOIDAL IMERSA EM UM MOLDE POROSO. DESSA FORMA, ESTE TRABALHO OBJETIVA DESENVOLVER UMA FORMULAçãO DE BARBOTINA COM PóS DE ARGILA GORDA EXTRAíDOS DAS REGIõES DE MOJU-PA E ICOARACI-PA. ALéM DISSO, OBTER PROPRIEDADES ADEQUADAS PARA A OBTENçãO DE CORPOS CERâMICOS VERDES ATRAVéS DA SEPARAçãO DA áGUA POR UM MOLDE DE GESSO, SEGUIDO DA SECAGEM NATURAL E EM ESTUFA A 100 ºC POR 4 H, E POSTERIOR AVALIAçãO DA SINTERIZAçãO A 800 ºC POR UM PERíODO DE 76 MINUTOS, PARA OBTENçãO DE PEçAS CERâMICAS PEQUENAS COM ESPESSURA DE PAREDES REDUZIDAS. OS RESULTADOS DEMONSTRAM QUE A COMPOSIçãO DA BARBOTINA SE MOSTROU EFICIENTE PARA A PRODUçãO DE CERâMICAS OBTENDO-SE PEçAS COM CARACTERíSTICAS E PROPRIEDADES QUE SE ASSEMELHAM AO ARTESANATO CERâMICO.

BARBOTIN IS A VERY INFLUENTIAL PROCESS FOR THE CERAMIC FORMING ACTIVITY AND IS WIDELY USED IN THE CERAMIC INDUSTRY TO PRODUCE MATERIALS USING THE GLUING METHOD. THIS PROCESS CONSISTS OF REMOVING THE LIQUID PART OF A COLLOIDAL SUSPENSION IMMERSED IN A POROUS MOLD. THEREFORE, THIS WORK AIMS TO DEVELOP A SLIP FORMULATION WITH FAT CLAY POWDERS EXTRACTED FROM THE REGIONS OF MOJU-PA AND ICOARACI-PA. FURTHERMORE, OBTAIN SUITABLE PROPERTIES FOR OBTAINING GREEN CERAMIC BODIES BY SEPARATING THE WATER USING A PLASTER MOLD, FOLLOWED BY NATURAL AND OVEN DRYING AT 100 ºC FOR 4 H, AND SUBSEQUENT EVALUATION OF SINTERING AT 800 ºC FOR A PERIOD OF 76 MINUTES, TO OBTAIN SMALL CERAMIC PIECES WITH REDUCED WALL THICKNESS. THE RESULTS DEMONSTRATE THAT THE SLIP COMPOSITION PROVED TO BE EFFICIENT FOR THE PRODUCTION OF CERAMICS, OBTAINING PIECES WITH CHARACTERISTICS AND PROPERTIES THAT RESEMBLE CERAMIC CRAFTS.