IMPACTO DOS MODIFICADORES DE RESINA EM PROPRIEDADES ESTRUTURAIS EPÓXI COM ADIÇÃO PARTICULADOS DE GRANITO

IMPACT OF RESIN MODIFIERS ON EPOXY STRUCTURAL PROPERTIES WITH ADDED GRANITE PARTICLES

Authorship

JÚNIOR, ROGÉRIO RABELLO DA ROCHA; CARVALHO LIRIO, JOSÉ LUCAS DECOTÉ DE; SIMONASSI, NOAN TONINI; DUARTE, FELIPE PERISSE LOPES; VIEIRA, CARLOS MAURÍCIO FONTES; MONTEIRO, SERGIO NEVES

JÚNIOR, ROGÉRIO RABELLO DA ROCHA

I am this author

CARVALHO LIRIO, JOSÉ LUCAS DECOTÉ DE

I am this author

SIMONASSI, NOAN TONINI

I am this author

DUARTE, FELIPE PERISSE LOPES

I am this author

VIEIRA, CARLOS MAURÍCIO FONTES

I am this author

MONTEIRO, SERGIO NEVES

I am this author

DOI

10.5151/2594-5327-41571

Downloads

Abstract

O ESTUDO VISA AVALIAR O COMPORTAMENTO MECâNICO DE COMPóSITOS VARIANDO A ESTEQUIOMETRIA "PHR" (PARTES DE ENDURECEDOR POR RESINA). UTILIZOU-SE RESINA EPóXI DGEBA/TETA, VARIANDO A QUANTIDADE DE ENDURECEDOR ENTRE 10% E 20% EM MASSA. OS RESíDUOS DE GRANITO FORAM TRITURADOS E INCORPORADOS à RESINA EM 45%. CORPOS DE PROVA FORAM MOLDADOS, CURADOS POR 24 HORAS E TESTADOS APóS UMA SEMANA PARA TRAçãO, COMPRESSãO E FLEXãO. OS RESULTADOS MOSTRARAM QUE A ADIçãO DE PARTíCULAS DE GRANITO REDUZIU A RESISTêNCIA à COMPRESSãO DOS COMPóSITOS EM COMPARAçãO COM A RESINA PURA. A ANáLISE ANOVA INDICOU QUE A VARIAçãO NA QUANTIDADE DE ENDURECEDOR NãO AFETOU SIGNIFICATIVAMENTE O MóDULO DE RUPTURA NOS COMPóSITOS, ENQUANTO PARA A RESINA PURA, A RESISTêNCIA AUMENTOU SIGNIFICATIVAMENTE A PARTIR DE 17,5% DE ENDURECEDOR. O MóDULO DE ELASTICIDADE NãO FOI SIGNIFICATIVAMENTE AFETADO PELA QUANTIDADE DE ENDURECEDOR. CONCLUIU-SE QUE O AUMENTO DE PHR NãO INFLUENCIOU SIGNIFICATIVAMENTE A RESISTêNCIA DOS COMPóSITOS, ENQUANTO A RESINA PURA APRESENTOU GANHOS DE DESEMPENHO A PARTIR DE 17,5% DE ENDURECEDOR. PARA ECONOMIA DE ENDURECEDOR, RECOMENDA-SE USAR 10% PARA COMPóSITOS, PROPORCIONANDO MAIOR TEMPO DE TRABALHO DEVIDO àS REAçõES EXOTéRMICAS.

THE STUDY AIMS TO EVALUATE THE MECHANICAL BEHAVIOR OF COMPOSITES BY VARYING THE “PHR” STOICHIOMETRY (PARTS OF HARDENER PER RESIN). DGEBA/TETA EPOXY RESIN WAS USED, VARYING THE AMOUNT OF HARDENER BETWEEN 10% AND 20% BY MASS. THE GRANITE WASTE WAS CRUSHED AND INCORPORATED INTO 45% OF THE RESIN. TEST SPECIMENS WERE MOLDED, CURED FOR 24 HOURS AND TESTED AFTER ONE WEEK FOR TENSILE, COMPRESSIVE AND FLEXURAL STRENGTH. THE RESULTS SHOWED THAT THE ADDITION OF GRANITE PARTICLES REDUCED THE COMPRESSIVE STRENGTH OF THE COMPOSITES COMPARED TO THE PURE RESIN. ANOVA ANALYSIS INDICATED THAT VARYING THE AMOUNT OF HARDENER DID NOT SIGNIFICANTLY AFFECT THE MODULUS OF RUPTURE IN THE COMPOSITES, WHILE FOR THE PURE RESIN, THE STRENGTH INCREASED SIGNIFICANTLY FROM 17.5% HARDENER. THE MODULUS OF ELASTICITY WAS NOT SIGNIFICANTLY AFFECTED BY THE AMOUNT OF HARDENER. IT WAS CONCLUDED THAT THE INCREASE IN PHR DID NOT SIGNIFICANTLY INFLUENCE THE STRENGTH OF THE COMPOSITES, WHILE THE PURE RESIN SHOWED PERFORMANCE GAINS FROM 17.5% HARDENER. TO SAVE HARDENER, IT IS RECOMMENDED TO USE 10% FOR COMPOSITES, PROVIDING LONGER WORKING TIME DUE TO EXOTHERMIC REACTIONS.

Keywords

Compósitos; phr; epóxi.

Composites; phr; epoxy.