INCORPORAçãO DE RESíDUO DE CAULIM E DE VIDRO DE GARRAFAS DE BEBIDAS NA PRODUçãO DE BLOCOS CERâMICOS PARA APLICAçãO EM OBRAS DE ENGENHARIA

INCORPORATION OF KAOLIN AND GLASS RESIDUE FROM BEVERAGE BOTTLES IN THE PRODUCTION OF CERAMIC BLOCKS FOR USE IN ENGINEERING WORKS

Authorship

LIRA, RODOLFO AUGUSTO DO ROSARIO; SILVA, ALISSON CLAY RIOS DA; CANDIDO, VERÔNICA SCARPINI; MATOS, TAIANA DE SOUSA; BRITO, FABIO MOREIRA

LIRA, RODOLFO AUGUSTO DO ROSARIO

I am this author

SILVA, ALISSON CLAY RIOS DA

I am this author

CANDIDO, VERÔNICA SCARPINI

I am this author

MATOS, TAIANA DE SOUSA

I am this author

BRITO, FABIO MOREIRA

I am this author

DOI

10.5151/2594-5327-41197

Downloads

Abstract

A INDúSTRIA DA MINERAçãO é UMA GRANDE GERADORA DE RESíDUOS E CONTRIBUI FORTEMENTE PARA A DEGRADAçãO AMBIENTAL. VISANDO UMA DESTINAçãO MAIS ECOLóGICA PARA O RESíDUO DO CAULIM E RESíDUO DE VIDRO PROVENIENTE DE GARRAFAS DO TIPO LONG NECK, ESTE TRABALHO TEM POR OBJETIVO A PRODUçãO DE BLOCOS CERâMICOS PARA OBRAS DE ENGENHARIA. NESTES ARTIGOS AS MATéRIAS PRIMAS FORAM BENEFICIADAS: SECAGEM, COMINUIçãO E PENEIRAMENTO (80 MESH), E POSTERIORMENTE HOUVE A MISTURA DAS MESMAS PARA A PRODUçãO DOS CORPOS DE PROVAS EM FORMATOS CILíNDRICOS. AS MATéRIAS-PRIMAS FORAM CARACTERIZADAS UTILIZANDO A TéCNICA DE CARACTERIZAçãO DE RAIOS-X (DRX), ENQUANTO OS CORPOS DE PROVAS FORAM SINTERIZADOS A 900°C, E POSTERIORMENTE FORAM SUBMETIDOS A ENSAIOS DE COMPRESSãO, ONDE ALCANçARAM VALORES MáXIMOS DE 72,20 MPA PARA AS AMOSTRAS PRODUZIDAS COM ARGILA E RESíDUO DE VIDRO, E 21,50 MPA, PARA AMOSTRA PRODUZIDA COM RESíDUO DE CAULIM E RESíDUO DE VIDRO.

THE MINING INDUSTRY IS A MAJOR GENERATOR OF WASTE AND CONTRIBUTES HEAVILY TO ENVIRONMENTAL DEGRADATION. AIMING FOR A MORE ECOLOGICAL DESTINATION FOR KAOLIN WASTE AND GLASS WASTE FROM LONG NECK BOTTLES, THIS WORK AIMS TO PRODUCE CERAMIC BLOCKS FOR ENGINEERING WORKS. IN THESE ARTICLES, THE RAW MATERIALS WERE PROCESSED: DRYING, COMMINUTION AND SIEVING (80 MESH), AND LATER THEY WERE MIXED TO PRODUCE THE SPECIMENS IN CYLINDRICAL FORMATS. THE RAW MATERIALS WERE CHARACTERIZED USING THE X-RAY CHARACTERIZATION TECHNIQUE (XRD), WHILE THE SPECIMENS WERE SINTERED AT 900°C, AND WERE SUBSEQUENTLY SUBJECTED TO COMPRESSION TESTS, WHERE THEY REACHED MAXIMUM VALUES OF 72.20 MPA FOR SAMPLES PRODUCED WITH CLAY AND GLASS RESIDUE, AND 21.50 MPA, FOR THE SAMPLE PRODUCED WITH KAOLIN RESIDUE AND GLASS RESIDUE.

Keywords

Argila; resíduo de caulim; resíduo de vidro; blocos de vedação.

Clay; Kaolin residue; Glass waste; Fence blocks.